【摘 要】本文针对钢铁零件磷化过程中，钢铁零件表面成膜时存在的主要缺陷问题;介绍了生锈泛黄泛绿、挂白色浮灰现象的产生，分析形成生锈泛黄泛绿、挂白色浮灰现象的原因;并根据缺陷现象的成因，提出预防和解决该问题的思路与方法。

【关键词】生锈泛黄泛绿;挂白色浮灰;缺陷成因;解决方法

中图分类号： TG174.4 文献标识码： A文章编号： 2095-2457（2019）17-0036-002

DOI：10.19694/j.cnki.issn2095-2457.2019.17.016

Cause Analysis and Solution of Phosphating Defect of Iron and Steel Parts

WU Wan-ping YAO Dian-min

（China Shipbuilding Industry Corporation N0.722 Research Institute， Wuhan Hubei 430079， China）

【Abstract】In this paper， the main defects existing in film forming on the surface of iron and steel parts during phosphating process are introduced， the occurrence of rust yellowing， greening and hanging white floating ash phenomenon is introduced， the causes of rust yellowing， greening and hanging white floating ash phenomenon are analyzed， and the ideas and methods to prevent and solve this problem are put forward according to the causes of the defects.

【Key words】Rusting; Yellowing; Greening; Hanging white floating ash; Causes of defects; Solutions

0 引言

鋼铁零件浸入磷化液（某些酸式磷酸盐为主的溶液），在表面沉积形成一层不溶于水的结晶型磷酸盐转换膜的过程，称之为磷化。磷化膜具有微孔组织，经填充、浸油或涂漆处理后，给基体金属提供保护，在一定程度上防止金属被腐蚀;用于涂漆前打底，提高漆膜层的附着力与防腐蚀能力;在金属冷加工工艺中起减摩润滑作用。磷化的优点在于可以实现在复杂零件内表面获得保护膜层。这是其它许多电化学方法无法实现的。因此，磷化工艺在金属防护领域得到了广泛的应用。

1 磷化的分类

磷化工艺可根据其磷化液的主要成分和成膜离子的种类分为：锌系、锰系和铁系等;根据磷化处理过程中，磷化液温度的高低又可以分为：高温、中温、常温磷化。

2 磷化的原理

磷化过程包括化学与电化学反应。不同磷化体系、不同基材的磷化反应机理比较复杂。科学家在这方面已做过大量的研究，随着对磷化研究逐步深入，当今各学者比较赞同的观点是磷化成膜过程为：将钢铁件浸入磷化液组成的酸性稀水溶液（PH值为1～3，溶液相对密度为1.05-1.10）中，酸的浸蚀使基体金属表面氢离子浓度降低，产生的氢原子;加入促进剂氧化掉所产生的氢原子生成水，进一步降低了金属表面氢离子的浓度。……