SXH70材料在魏家堡水电站中的应用

马艳丽

(杨凌职业技术学院， 陕西 杨凌 712100)

摘要：SXH70材料的抗磨蚀性能是不锈钢X5CrNi13-4的91.5倍；抗空蚀能力是不锈钢X5CrNi13-4的1.55倍，该材料在魏家堡电站的导叶和转轮表面进行高速火焰喷涂，提高了水轮机的效率，稳定了机组的出力，延长机组的大修周期。实验证明了SXH70材料是一种有效的解决泥沙磨蚀和空蚀联合作用的表面防护材料。

关键词：SXH70材料； 水轮机； 磨蚀； 魏家堡电站； 高速火焰喷涂

收稿日期：2015-03-24

作者简介：马艳丽(1976-)，女，陕西蓝田人，讲师，主要从事水利水电动力工程专业的教学与科研工作。

中图分类号：TK730.8

Application of SXH70 Material in Weijiabu Hydropower Station

MA Yan-li

(Yangling Vocational and Technical College, Yangling, Shaanxi 712100, China)

Abstract:The cavitation erosion and the abrasion resistance of SXH70 material were 1.55 times and 91.5 times that of X5CrNi13-4 stainless steel. Through spraying SXH70 material on the guide vane and runner surface of turbine, Weijiabu Hydropower Station improved the efficiency of turbine, and stabilized the unit of output of turbine, shortened the period of checking and repairing of turbine. The result proved that SXH70 material is an effective surface protection material to resist the combined effect of silt abrasion and cavitation.

Key words: SXH70 material ;turbine；abrasion；Weijiabu Hydropower Station；high velocity oxygen flame

1前言

宝鸡峡魏家堡水电站处于渭河中下游，长期以来泥沙的磨蚀使该电站水轮机的过流部件损害严重，特别是宝鸡峡渠首加闸、加坝工程前，转轮、导叶等过流部件磨蚀严重，检修费用高达90多万。由于磨蚀造成水轮机的效率急剧下降；机组振动、摆度严重超标；导叶、止漏环漏水加大，机组无法实现正常停机和迅速并网[1]。因此不得不进行拆卸大修和技术改造。为了解决泥沙的磨蚀问题，电站多次进行研究和试验，通过对各种材料的比对和筛选，最终选用高速火焰喷涂SXH70材料，成功的解决了机组转轮和导叶的磨蚀问题。

2SXH70材料的性能

SXH70喷涂材料是由西北电力试验研究院和瑞士苏尔寿公司合作开发的产品。该涂层是用HVOF热喷涂的方法在钢材上制取厚度为0.2～0.5 mm厚的碳化钨-钴金属陶瓷涂层。涂层表面粗糙度为1.6 μm；涂层密度为13 500 kg/m3； 涂层的显微硬度在1 300～1 500之间(300 kgf负荷)；……