Effect of Impregnation Technology on Properties of Poplar Reconstituted Wood

CUI Lidong1HE Dan² ZHANGYe1LIU Haoyang1HANGHaibing** （1.Heilongjiang Provincial Institute of Wood Science，Heilongjiang Harbin 15oo81；2.Harbin Far East Institute of Technology，Heilongjiang Harbin ）

AbstractEffects of impregnation concentration，impregnation time and impregnation temperature on static bending strength and elastic modulus of poplar reconstituted wood were studied.it was showed impregnation concentrationand impregnation time have litle influence on the static bending strength，and elastic modulus was increasing firstly and then decreasing by experimental results.static bending strength was increasing firstly and then decreasing with impregnation temperature，but impregnation temperature has little influence on the elastic modulus.

Key wordsphenolic adhesive；recombinant wood；impregnation

重组木的设想起源于1973年[1-3]，是80年代由澳大利亚首创的一种新型人造实体木材[4]，它是将速生小径材、枝丫材及制材边角料等廉价质地材料经碾搓设备加工成横向不断裂，纵向松散而又交错相连的网状木束，再经干燥、铺装、施胶和热压而制成的[5]。杨木是我国主要的速生树种，由于材质软、易变形，难以直接实木化利用，而重组木作为杨木高效、高值化利用的重要途经之一[6]。

重组后的木材性能提升明显，可以有效的提高物理力学性能如强度、硬度、尺寸稳定性等。通过重组材技术加工成高性能材料后，可以替代部分昂贵的实木或其他合成材料，提高产品的附加值，为企业带来更大的经济效益。本文主要以酚醛胶粘剂浸渍杨木制作成重组材，着重研究了浸渍浓度、时间和温度对重组材性能的影响。

1实验材料与方法

1.1实验材料与设备

杨木木条：长 500mm. 宽 15mm 厚 1.8mm ，含水率 8% 。

酚醛树脂胶粘剂，自制，固体含量 46% ， pH 值11.15。

压机，天平，烘箱，冷压模具，带锯，力学试验机等。

1. 2 工艺流程

干燥 $$ 称重 $$ 浸胶 $$ 组胚 $$ 热压 $$ 试件处理具体步骤：将杨木木条干燥，使干燥后木条含水率控制约 8% ;每个试件用木条统一称重，使试件重量一致；将木条按照实验设计方案常压浸渍；浸渍后在 50% 烘箱中烘干；采用手工顺纹铺装方式组胚，放入模具中热压，成型。在室温条件下放置两天，制成规定尺寸试件。

1.3 实验设计

采用均匀设计方法，以浸渍浓度、浸渍时间以及浸渍温度为实验的三个因素，研究重组木弹性模量和静曲强度的影响。……