高颖 梁丽丰

摘  要：某核电厂安全厂房海水系统使用阀门为止回阀，于2018年机组商运初始发现阀门泄漏缺陷，对同厂家生产的同机组19台阀门解体检查，发现14台阀门进出口法兰面均存在不同程度的腐蚀缺陷，同时引起了止回阀阀杆轴套破损，影响了机组安全稳定运行。本文结合该核电站阀门的结构、材质和运行工况等方面，分析了核电站海水系统阀门法兰发生的主要腐蚀机理，并有针对性的提出了相应的解决措施，以期为同类设备的腐蚀防护工作提供借鉴。

关键词：核电站  缝隙腐蚀  金属修补  垫片

中图分类号：TM623                          文献标识码：A                  文章编号：1674-098X（2021）01（a）-0024-03

Abstract：The check valves are used in the seawater system of a nuclear power plant safety plant， valve leakage defects were discovered at the beginning of the unit commercial operation in 2018. We inspect the disassembly of 19 valves of the same unit produced by the same manufacturer and find that 14 valves have different degrees of corrosion defects on the flange surfaces of the inlet and outlet of the valves. At the same time， it causes the check valve stem bushing to be damaged， which affects the safe and stable operation of the unit. This article combines the structure， material and operating conditions of the nuclear power plant valve， analyzes the main corrosion mechanism of valve flanges in the seawater system of nuclear power plants， and proposes corresponding solutions in a targeted manner. It is expected to provide a reference for the corrosion protection of similar equipments.

Key Words：Nuclear power plant; Crevice corrosion; Metal repair; Gasket

某核电站机组二期于2018年初投入商业运行，每台机组安全厂房海水系统主要包括厂用水机械清洁系统、重要用户用水系统和柴油发电机厂用水系统，系统主要功能是在非正常工况下为中间回路提供冷却水，以保证机组的安全稳定运行。机组商运不久，运行现操在巡检过程中发现海水系统止回阀外漏，待进行设备解体后发现止回阀进出口法兰及配对法兰均存在大范围的腐蚀凹坑，腐蚀主要特点为：（1）腐蚀缺陷主要出现在法兰与金属缠绕垫接触部位;（2）位于法兰中部偏下侧的腐蚀凹坑较为严重;（3）腐蚀样貌为长条装凹坑，最深处可达2mm;（4）金属石墨缠绕垫上的金属带发生部分溶解、断裂。为了研究阀门法兰发生腐蚀的主要机理，对阀门法兰及垫片材质进行了调研，同时结合系统运行工况，对阀门发生泄漏的原因进行了分析。……