刘美红 牛高峰 张康熙

摘 要：本文针对长行程缸筒的刚度差、对加工设备的要求高、零件加工精度难以保证等问题进行改进。针对这些问题，本文首先分析缸筒的技术参数要求，然后提出三种缸筒工艺改进方案，最后从制造成本、生产效率、壁厚强度三方面对这三种改进工艺进行对比分析。结果表明，方案3的综合优势明显。

关键词：长行程缸筒;加工工艺;改进

中图分类号：TD355.4文献标识码：A文章编号：1003-5168（2019）16-0062-03

Abstract： Aiming at the problems of poor stiffness of long stroke cylinder， high requirement of processing equipment and difficult guarantee of parts processing accuracy， this paper improved the design. In order to solve these problems， this paper first analysed the technical parameters of cylinder， then put forward three kinds of cylinder process improvement schemes， and finally made a comparative analysis of the three improved processes from three aspects： manufacturing cost， production efficiency and wall thickness strength. The results show that the comprehensive advantages of scheme 3 are obvious.

Keywords： long stroke cylinder;processing technology;improvement

缸筒是液压缸的核心部件，其与缸底、活塞等零件构成一个封闭的容腔，在压力油的作用下推动活塞沿缸筒内壁运动。设计缸筒时，不仅要保证油缸的压力、速度、行程和安装距，还必须保证其具有足够的强度和刚度，以抵抗液压力和其他外力作用。

1 缸筒的技术参数要求

臂架伸缩液压缸缸筒如图1所示，材料为45号钢，内径精度为H9，圆度为0.04，缸筒内表面光洁度[Ra]最大为0.4μm，长度为7 630mm，长度与内径比[LD]=42.4，要求最大壁厚与最小壁厚差不大于1mm。

2 缸筒的工艺改进方案

长行程液压缸缸筒的加工难点是缸筒自身的薄壁及超长原因导致其刚度差且原材料质量差异明显。针对上述问题，综合考虑市场上几种常用钢管的性能及价格，设计时对符合《结构用无缝钢管》（GB/T 8162—2008）规定的45号热扎钢管和45号精密冷拔钢管进行试验。初步拟定了3种缸筒加工方法，如图2所示，方案1为常用加工方法。

2.1 方案1

选用45号热扎无缝钢管毛坯料Φ219mm×24mm×7 636mm。由于毛坯在轴向上呈波浪形，在径向上呈不规则多边形，以及壁厚不均匀等缺陷，需要在压力机上进行校直，使其直线度控制在0.5mm/m内。……