摘要： 本文采用PEO技术在钛衬底上制备了一层致密的TiO2陶瓷薄膜，并对其形成机理进行了探讨。利用X—射线衍射分析（XRD）和扫描电子显微镜（SEM）研究了陶瓷薄膜的结构特性，并利用电化学极化测试技术分析了陶瓷薄膜的腐蚀特性。研究表明，利用PEO技术在钛衬底上生成陶瓷氧化膜后，其耐腐蚀性能优良，而且经65%～68%的发烟硝酸浸泡72小时后，其耐腐蚀性能得到进一步提高，可以作为腐蚀类军用危险品的包装材料使用。

Abstract： In this paper， compact TiO2 oxide ceramic thin films were prepared on Ti pieces by plasma electrolytic oxidation （PEO） technic. The mechanism of the forming process was also explored. By using x-ray diffraction （XRD）， scanning electron microscope （SEM） and electrochemistry analytical instrument， the structural properties， micrographs and corrosive characteristics of the samples were studied. The result shows that TiO2 ceramic oxide thin films formed on Ti pieces by plasma electrolytic oxidation （PEO） technic have fine corrosion-resisting capability， and after marinated in 65%～68% fuming nitric acid 72 hours， their corrosion-resisting capability could be improved farther，so that they could be used as packaging materials for causticity military dangerous goods.

关键词： PEO技术；陶瓷氧化膜；军用危险品；包装材料

Key words： PEO technic；ceramic oxide film；military dangerous goods；packaging materials

中图分类号：TJ08 文献标识码：A 文章编号：1006-4311（2017）05-0082-03

0 引言

军用危险品是指用于国防和军事目的，具有爆炸、易燃、毒害、腐蚀和放射等特性，在运输、装卸和贮存过程中，容易造成人员伤亡和财产毁损，必须进行特别防护的物品[1]。《军用危险货物铁路运输规则》中，将军用危险货物（即军用危险品）分为9类43项，其中的第八类为腐蚀品。腐蚀品是指能通过化学作用使生物组织接触时会造成严重损伤或在渗漏时会严重损害甚至毁坏其他货物或运载工具的物质。主要包含与完好皮肤组织接触不超过4h（小时），在14d（天）的观察期中发现引起皮肤全厚度损毁，或在温度55℃时，对S235JR+CR型或类似型号钢或无覆盖层铝的表面均匀年腐蚀率超过6.25mm/a的物质[2]。其主要品种为酸类和碱类。腐蚀品一旦泄露，非常容易引起燃烧，甚至爆炸，造成伤亡，因此，腐蚀品包装有着严格的技术要求。由于不同腐蚀品对不同材料的腐蚀作用千差万别，因此，对腐蚀品包装材料的要求更为复杂。……