周俊建

摘要 本文根据硅锰铝合金的特点,在鉴定硅锰铝合金中硅的过程运用了酸碱滴定法,实验中利用氟硅酸钾溶解于沸水中生成氢氟酸的原理。试样以硝酸、氢氟酸溶解,硅转化为硅氟酸,,加入硝酸钾生成氟硅酸钾沉淀。经过滤、洗涤沉淀中的游离酸后,溶解于中性沸水中,生成氢氟酸,以溴麝香草酚蓝为指示剂,用氢氧化钠标准溶液滴定游离出的氢氟酸,借此测定硅锰铝合金中硅含量,其相对标准偏差小于0.0796%。

关键词 硅锰铝合金;鉴定方法;实验分析

中图分类号 O6-31文献标识码 A文章编号 1674-6708(2009)10-00072-02

Abstract This article based on the characteristics of aluminum alloy mnsi, in the identification of mnsi aalloy silicon process use of acid-base titration. Experiments using potassium chemonucleolysis in boiling water generated in the principle of hydrofluoric acid. Nitric acid, hydrofluoric acid rheomolding to ,chemonucleolysis Silicon into a silicofluoric acid, by adding potassium generated by metathetical. The filtered, washing the free acid precipitation in , after the chemonucleolysis neutare; generated hydrofluoric acid to bromamine to shexiang agrimopholum pentaphyllum , indicator detrmincd with a sodium hydroxide standard solution free of hydrofluoric acid, and take this determination of mnsi aalloy SI , showing the relative standard deviation of less than 0.0796%.

Keywords Mnsi aluminum alloy,Identification of methods,Experimentalanalysis

0 引言

近年来,铝合金的生产使用比较广泛,各种铝合金的质量也引起大众的关注,现在介绍一种硅锰铝合金中硅的检测方法。硅锰铝合金是由硅、锰、铝及少量铁组成的合金,合金中的硅、锰、铝与氧的亲和力最强,是硅锰铝系合金中较好的脱氧剂、脱硫剂,具有熔点低、颗粒大、容易上浮、脱氧效果好等优点,使钢中的氧降到最低,同时形成含硅、锰、铝的复杂氧化物易从钢液中上浮,纯净钢液,提高钢的质量和加工性能等。因此,开展测定硅锰铝合金中主量化学元素的分析具有重要意义。

1 实验部分

1.1 试剂

硝酸:ρ=1.42 g/mL;氢氟酸:ρ=1.15 g/mL;硝酸钾饱和溶液;过氧化氢:30%;硝酸钾洗涤液:称取100 g硝酸钾溶解于900 mL水中,加入100 mL乙醇,混匀;溴麝香草酚蓝为指示剂:1%的乙醇溶液;尿素:固体;氯化钾:固体;氢氧化钠标准溶液: 0.25 mol/mL。

1.2 实验方法

称取0.2000 g试样于200 mL塑料杯中,加10mL硝酸,缓慢滴加5mL氢氟酸,摇动均匀,在室温下溶解1min后,加1g尿素,加2mL过氧化氢摇动30s,放置2min,加2 g氯化钾,加20mL硝酸钾饱和溶液,加少许滤纸浆,搅拌匀,放置12min,使氟硅酸钾沉淀完全。……