【摘要】 不锈钢螺丝是机械装配、紧固等必不可少的器件之一，不锈钢螺丝锁死问题在工程施工过程中经常发生，为了更好地解决此类问题，分别从材质，故障原因、解决措施等多个方面进行分析，针对不同情况提出相应的改进措施。

【关键词】 不锈钢;螺丝;锁死;措施

【DOI编码】 10.3969/j.issn.1674-4977.2021.06.021

Analysis and Solution of Locking Problem of Stainless Steel Screw

WANG Hui1，WEI Wei-hua1，ZHU Ling-chao1，LIU Xiao-li1，WU Hui-en2

（1.Shanxi Xinhua Chemical Defense Equipment Research Institute Co.，ltd.，Taiyuan 030008，China;2.Anti chemical warfare Military Representative Office of the anti chemical warfare military representative Bureau of the Army Equipment Department of the Chinese people's Liberation Army in Taiyuan，Taiyuan 030006，China）

Abstract： Stainless steel screw is one of the indispensable devices for mechanical assembly and fastening. The locking phenomenon of stainless steel screws often occurs in the process of engineering construction. In order to better solve this kind of problem，this paper analyzes from the aspects of material，fault causes and solving measures，and puts forward corresponding improvement measures for different situations.

Key words： stainless steel;screw;locking;measures

在日常生活和工業生产制造中，螺丝作为必不可少的标准件为我们的生活和生产带来了很大的便捷。但是，在使用过程中也存在一些不足，尤其在装配过程中时有发生不锈钢螺丝锁死现象，这让工程技术人员头痛不已。其主要表现为螺丝紧固过程中出现黏着现象，导致拆卸困难或无法紧固，最终使设备的维护、维修受到影响。在金属件连接过程中，也存在不锈钢螺丝锁死的问题。鉴于这些情况，我们结合日常过程中产生的问题进行了系统分析，针对不同的问题提出了处理措施。

1 不锈钢螺丝的材质

不锈钢螺丝按照性能等级分为：45、50、60、70、80;按照不锈钢材质分为：奥氏体、马氏体、铁素体等。

1.1 奥氏体不锈钢

奥氏体不锈钢是碳与合金元素在γ-Fe中溶解所形成的固溶体，状态依然保持着γ-Fe的面心立方晶格结构。奥氏体是一般钢在高温条件下的组织，其存在有一定的温度和成分范围。有些淬火钢能让一部分奥氏体保持到室温，通常这种奥氏体叫残留奥氏体。奥氏体大多数由等轴状的多边形晶粒组成，晶粒内部存在孪晶。在加热转变快要结束的时候奥氏体晶粒比较细小，晶粒边界呈无规则状的弧形。……