王金霞 杨中娜

摘要：本文主要是针对某油田平台出井油管腐蚀失效的问题，采用了力学性能分析、化学成分分析、宏观分析等技术手段，并结合该出井油管的实际工况，对其失效的原因进行了研究分析。根据理化性能分析，出井油管材质合格，根据宏观形貌分析和历年分析报告，油管外壁存在均匀的CO2腐蚀，并覆盖有单质硫S8，局部位置可能因接触电缆导致电偶腐蚀，产生了点蚀坑。

关键词：CO2腐蚀 失效分析 低硫原油 S8

Study on Corrosion Failure of Well Tubing

WANG Jinxia YANG Zhongna

（CNOOC （Tianjin） Pipeline Engineering Technology Limited Company，

Tianjin， 300450 China）

Abstract： This paper is mainly aimed at the failure analysis of corrosion perforation of stainless steel liquid control line of an offshore platform. By means of macro analysis， chemical composition analysis， metallographic analysis， and combined with the actual working conditions of the stainless steel liquid control pipeline， the failure causes are analyzed. According to the analysis of physical and chemical properties， the material of well tubing is qualified. According to the analysis of macro-morphology and local composition， CO2 corrosion was uniform on the outer wall of the tubing and covered with elemental sulfur S8.

Key Words： CO2 corrosion; Failure analysis; Stainless steel; S8

1现场工况

某油田某井检泵作业，发现一根出井油管腐蚀严重，深度位于192 ～202m，现场照片如图1所示。同时本井电泵控制电缆外铠皮也腐蚀较严重，出井电缆铠皮，用手即可碾碎。

此井开发完井层段L20-L100，采用压裂充填完井方式。该井下入井下机组：77级TE4200电潜泵;1个538系列MAGS3气体分离器;2节513系列保护器;1节E56-09 （250HP，2355V，64A）电机;Zenith E7 MK2井下传感器。

该井于2015年7月30日上线，上线后日产油79.5m³/d，含水10%。

2019年12月18日此井于21∶23故障停井，经电气人员检查VFD报警为马达阻转，电气人员测得三相直阻分别为3.7/3.7/3.7Ω，绝缘为0;转矩设定值为0.6，调整相序尝试反转启泵。22∶08反转启泵，启泵失败，VFD报警为DC LINK OC HW（中性点过电流故障），对变频器进行门极测试和参数检查，无异常，电气人员将转矩设定值改为0.8，调整相序为正转。对该井进行环空打水冲洗19m³/h。22∶38正转启泵，启泵失败，VFD报警仍为DC LINK OC HW（中性点过电流故障），电气人员测得三相直阻分别为9.6/6.4/1.5Ω，三相直阻不平衡，絕缘为0。

2 内外壁宏观分析

观测腐蚀穿孔油管的外壁形貌特征，多处明显存在大小不……