周忠长

摘 要：对紧凑型SUV车发盖电泳二次流痕缺陷的形成原因进行了描述和分析，探讨了导致紧凑型SUV车发盖电泳二次流痕缺陷形成的机理。主要从涂装工艺、车身产品结构以及工件夹层涂黑胶工艺等多方面对电泳二次流痕缺陷形成进行探讨和分析，并提供了一些预防及解决方法。

关键词：汽车涂装 发盖 电泳二次流痕 缺陷防控

A Discussion on the Causes and Solutions of Secondary Flow Marks in the Hair Cover of Compact SUV

Zhou Zhongchang

Abstract：The reason for the formation of the secondary flow mark defects in the hood of a compact SUV is described and analyzed， and the mechanism leading to the formation of the secondary flow mark in the hood of a compact SUV is discussed. It mainly discusses and analyzes the formation of electrophoretic secondary flow mark defects from many aspects such as painting process， body product structure and workpiece interlayer coating black glue process， and provides some prevention and solution methods.

Key words：automobile coating， hair cover， electrophoresis secondary flow mark， defect prevention and control

1 前言

汽车涂装车身电泳的工艺流程一般为：电泳─UF喷洗─UF循环喷洗─UF浸洗─新鲜UF喷洗─循环DI水浸洗─新鲜DI水喷洗─沥水─烘烤。其中，UF即用半透膜强制过滤槽液（Ultra Filtration）。从UF装置中析出的透明液是UF液，UF液的主要成分是水，另外还有水溶性溶剂、水溶性低分子树脂、中和剂、Na、Pb等离子。DI即去离子水（Deionized Water），是利用RO反渗透+混床原理除去水中99%以上的杂质和各种阴、阳离子，使水质达到一定的纯度。

电泳涂膜二次流痕是汽车涂装生产中常见的涂膜弊病之一，其现象为通常电泳涂膜烘干过程中发生于车身的钣金搭接夹缝结构处，在电泳、后冲洗、沥水进入烤房前湿电泳涂膜表面正常，但经烘烤后流出形成流痕并污染在車身外观面时（见图1），之所以称其为二次流痕，其特点是一旦发生，频次就很高接近100%。当二次流痕出现在总装后的外露面时，就会影响下道工序中涂层的成膜质量，为了消除其不良影响，一般会对电泳涂层缺陷进行打磨处理。

2 现状调查：

2.1 紧凑型SUV车在某生产线生产发盖前端电泳二次流痕问题PPH值92%，对车身外观质量造成影响。

3 紧……