摘要：  针对某单层工业厂房屋面预应力混凝土双T板端部开裂情况，利用有限元软件Abaqus进行计算分析，发现双T板支座端部存在构造不佳、易出现初始裂缝的问题，在施工过程中未按照构造要求施工、使用过程中温度变化等产生的不利效应对双T板受力影响不能忽略。针对双T板存在的问题提出处理措施，对已有开裂构件进行加固，处理效果良好。

关键词：  预应力混凝土板; 双T板; 腹板; 裂缝; 有限元

中图分类号：  TU378; TB115.1文献标志码：  B

Crack analysis and reinforcement on end of

prestressed concrete double-T used on roof

LIU Zhichun， LIU Junyu

（School of civil engineering， Shandong Jianzhu University， Jinan 250101， China）

Abstract： Aiming at the cracking of the prestressed concrete double-T plate on the roof of a single-storey industrial plant building， the finite element software Abaqus is used to analyze the double-T plate. It is found that there are some problems such as poor structure detailing and easily cracking at the end of the support. The influence of    the arrangement process during construction and the effect of temperature during service period cannot be ignored. In view of the existing problems， the improvement measures are proposed， and the existing components with cracks are reinforced. The treatment results are achieved.

Key words： prestressed concrete plate; double-T plate; web; crack; finite element

收稿日期：  2021-10-11修回日期：  2021-10-26

作者简介： 刘之春（1969—），男，山东莒县人，副教授，博士，研究方向为现代预应力结构、高层建筑结构，（E-mail）liuzhichun99@ sdjzu.edu.cn;

刘军宇（1996—），男，山东济南人，硕士研究生，研究方向为预应力结构，（E-mail）2019015125@stu.sdjzu.edu.cn0引言20世纪50年代，双T板由美国人设计而成，自20世纪90年代引进国内以来，因其结构轻巧、材料用料较少、可以实现较大的结构跨度，且双T板通过预制构件的标准化工业生产，可有效解决施工现场参差不齐的质量问题，提高标准化程度、施工速度以及劳动效率，在国内得到广泛应用。在双T板引入国内应用过程中，各地根據自身情况编制相应标准，但双T板在使用过程中端部产生裂缝的现象也较为普遍。国内外主要通过理论计算、试验及有限元模拟分析的方法对双T板进行承载力、裂缝以及相应构造措施的研究[1-5]。施桂保[6]对24 m及以上较大跨度的双T板出现裂缝的原因进行分析，统计得出80%以上的裂缝产生都源自于放张裂缝与温度裂缝，并从施工角度提出裂缝控制措施。……