王文君 李晓军 王新 马佳琨 李有华 贾小玉

摘 要：对SP-700合金的热处理强化效应研究。采用不同的热处理温度、固溶时效制度处理，分析热处理对合金组织及性能的影响。当合金在490～550℃固溶时效时，硬化效果较明显，塑性急剧降低。800℃固溶时效后的强度要高于850℃固溶时效后的强度。固溶处理后的SP-700合金性能取决于β相的特性或β相转变后的相的组成。

关键词：SP-700合金；热处理；组织；性能

中图分类号：TG166.5 文献标志码：A 文章编号：2095-2945（2018）29-0109-03

Abstract： The strengthening effect of heat treatment on SP-700 alloy was studied. The effect of heat treatment on the microstructure and properties of the alloy was analyzed using different heat treatment temperature and solution aging treatment. When the alloy is dissolved and aged at 490，550 ℃， the hardening effect is obvious and the plasticity decreases sharply. The strength after solution aging at 800 ℃ is higher than that after solution aging at 850 ℃. The properties of SP-700 alloys after solid solution treatment depend on the characteristics of β phase or the phase composition after β phase transformation.

Keywords： SP-700 alloy； heat treatment； microstructure； properties

1 概述

钛合金因其密度小、强度高和抗腐蚀性强等优点，已广泛应用于航空航天工业[1]。虽然Ti-6Al-4V合金因其具有较强的疲劳抗力和较好的断裂韧性，是目前最常用的钛合金，但是，由于其加工性能和可热处理性能都不太好，故加工成形困难、材料利用率低，导致它在能源和运输等非航空与航天领域的应用受到限制[2]。SP-700是为了克服Ti-6Al-4V合金的诸多缺点而研制的一种新型富β的（α+β）钛合金。此合金的超速成形型、抗拉强度、疲劳强度和断裂韧性等都得到了改善。

本文主要对SP-700合金板材热处理工艺进行研究。通过不同的热处理参数，对比组织和性能的变化。

2 实验

2.1 试验材料

SP-700合金采用真空自耗电弧熔炼，经锻造，制备成板坯。采用热差分析法测得的合金相变点温度为（900 ℃）。其化学成分见表1

2.2 实验方案

板坯在1200mm轧机热轧、冷轧，制成δ2mm板材，对硬态SP-700板材采取不同温度固溶处理：670℃～840℃，保温时间30′空冷。固溶时效处理：800℃固溶+490℃～550℃/4h时效；850℃固溶+490℃～550℃/4h时效。

3 结果与分析

3.1 固溶温度对合金组织及性能的影响