刘娜 邹清鹏 陈猛 庞洪

摘要：本文从钛带卷冷轧表面形貌的演化过程说明，表面形貌是影响冷轧钛带卷总体质量的一个重要方向，带卷总变形量大于60%时，随着变形量的增加，表面粗糙度趋于均匀一致（Ra≤0.4μm），可满足苛刻的成型条件；但当总变形量小于60%时，随着变形量的缩小，因表面粗糙度大（Ra>0.4μm），成型性能變差，不利于产品成型。

关键词：钛带卷；表面形貌；变形量

Abstract：this article from the coil cold-rolled titanium surface morphology of the evolutionary process，the overall quality of titanium surface topography is affect the cold rolled coil is an important direction of coil when the total deformation is greater than 60%，with the increase of the deformation，the surface roughness tends to be uniform and consistent，which can meet the demanding molding conditions.However，when the total deformation amount is less than 60%，as the deformation amount shrinks，the surface roughness is large and the molding performance is poor，which is not conducive to product molding.

Key words：Titanium coil Surface morphology The deformation

1引言

2010前我国钛带卷工业化生产处于空白，钛带卷完全依赖进口，而国外生产商也瞄准形式，持续抬高钛带卷的出口价，以此来抑制我国钛带的生产[1]。近年来随着国内宝钛集团、洛阳双瑞、湘投金天等企业先后建成钛带生产线，国内钛带材发展速度突飞猛进，现已可以向客户稳定提供厚度0.3～4.75mm冷轧钛带卷。

此前我们对钛带卷组织、性能、退火制度等都做了研究，而针对钛带卷冷轧表面形貌演化过程，至今还无专业的深入研究，但实际供货过程中却出现了一些因表面形貌问题导致的成型开裂现象，造成客户使用受限。基于以上原因，我们将开展钛带卷冷轧表面形貌研究，为后续更深层次的研究打好基础。

2试验

2.1试验材料

试验材料为经抛丸酸洗进行表面除氧化皮的热轧带卷一卷，尺寸规格为5.0mm×1000mm×C，通过20辊可逆式冷轧机分别进行10%，20%，30%，40%，50%，60%，70%和80%冷轧变形后，进行取样。

2.2试样制备

试样为每个变形量取试样两个，规格80mm×80mm，进行表面形貌观察及粗糙度测量。

2.3试验方法

2.3.1采用WYSX-40×倍放大镜进行表面形貌观察，使用手持相机进行拍照，每组试样拍两张照片，对比观察，取表面形貌清晰、典型照片进行分析。