袁洁 贺江平 胡晓侠 冯娜

摘 要：采用自制有機硅聚氨酯整理剂对棉织物进行处理，通过探究轧余率、整理剂用量、预烘温度、焙烘温度和焙烘时间对自制有机硅聚氨酯整理剂在棉织物上应用效果的影响，测试织物手感、白度、强力、抗皱性、亲水性等指标。结果表明：与市售氨基硅油柔软剂SOFT8468的应用对比，织物手感高半级，抗皱性，耐洗性更优。

关键词：棉织物；有机硅聚氨酯整理剂；手感；抗皱性

中图分类号：TS195.5

文献标志码：A

文章编号：1009-265X（2018）02-0066-05

Polyurethane Silicone Copolymer Applied Research on Cotton Fabric

YUAN Jie， HE Jiang ping， HU Xiao xia， FENG Na

（School of textile and materials， Xian Polytechnic University， Xian 710048， China）

Abstract：Self-made organic silicon polyurethane finishing agent was used to treat cotton fabrics. The influence of pickup， dosage of finishing agent， pre-heating temperature， baking temperature， and baking time on the application effect of self-made organic silicon polyurethane finishing agent in cotton fabrics was studied to test the hand feeling， whiteness， strength， wrinkle resistance， and hydrophilicity of textiles. The results show that the self-made organic silicon polyurethane finishing agent is superior to amino silicon oil softening agent SOFT8468 on the market in respect of hand feeling （half grade higher）， wrinkle resistance， and washability.

Key words：cotton； polyurethane modified silicone copolymer； process

天然纤维、合成纤维在染整加工过程中因机械摩擦作用导致织物起毛、手感变差[1]，因此可提升织物手感、滑爽性的柔软剂应运而生，其中效果优异的为有机硅类柔软剂：无毒无害，绿色环保、成本较低并且柔软效果优异、耐久性好，因此有机硅类柔软剂为织物后整理助剂中的主流产品[2]。水性聚氨酯链上含有亲水基团，因此形成的涂膜耐水性差，常需要改性。目前改性方法有交联、共混、共聚、纳米技术等，而采用有机硅改性聚氨酯是当前的研究热点之一[3-5]。本实验采取共聚的方法合成聚氨酯有机硅共聚物。

1 实 验

1.1 材料和仪器

织物：精纺纯棉平纹蚀磨布，176 g/m2，152×132根/10 cm（安徽华茂纺织股份有限公司）。

试剂：聚氨酯有机硅共聚物（自制），氨基硅油柔软剂SOFT8468（市售，清远精细化工有限公司），八甲基环四硅氧烷（D4，工业品，济南谷瑞特化工有限公司），四甲基氢氧化铵（分析纯，上海中锂实业有限公司），二正丁胺（化学纯，研域化学试剂有限公司），环氧封头剂……