摘要：通过锥入度试验、布氏黏度试验和DSR试验，对电气石改性沥青胶浆的高温性能进行了研究，分析电气石目数、掺量以及粉胶比对电气石改性沥青胶浆锥入度、黏度以及60 ℃流变性能的影响。研究表明：随着电气石掺量、目数以及粉胶比的增大，电气石改性沥青胶浆的锥入度逐渐减小，而布氏黏度逐漸增大； 60 ℃的车辙因子随着电气石掺量、目数和粉胶比的增加而不断增大。

关键词：电气石；锥入度；黏度；粉胶比

中图分类号：U416.217文献标志码：B

Abstract： The high temperature performance of tourmaline modified asphalt mortar was studied by cone penetration test， Brookfield viscosity test and DSR test. The influence of tourmaline mesh， content and fillerasphalt ratio on the cone penetration， viscosity and rheological properties at 60 ℃ of tourmaline modified asphalt mortar were analyzed. The results show that with the increase of tourmaline content， mesh and the fillerasphalt ratio， the cone penetration of tourmaline modified asphalt mortar gradually decreases， while its Brookfield viscosity gradually increases. The rutting factor at 60 ℃ also increases with the increase of tourmaline content， mesh and the fillerasphalt ratio.

Key words： tourmaline； cone penetration； viscosity； fillerasphalt ratio

0引言

沥青改性剂材料多为聚合物、树脂类等，虽然改性效果良好，但是制备工艺复杂且价格昂贵，大大提高了生产成本；而无机材料具有来源广泛、价格低廉等特点，从而得到越来越多公路工作者的青睐[13]。目前已经被广泛研究的无机改性剂有纳米CaCO3、石灰、硅藻土、矿质纤维与填料、蒙脱土、粉煤灰、水泥等[49]。虽然这些无机改性剂能够在一定程度上改善沥青路用性能，但也存在很多缺陷。以石灰为例，它能够有效改善沥青混合料的高温抗变形能力，但是会使其水稳定性能严重劣化，影响路面的使用寿命。因此，研发廉价且性能优异的无机改性剂是非常必要。石鑫等研究了不同类型电气石粉对沥青的改性作用，结果表明电气石粉能够显著提高改性沥青的路用性能，且赋予了其良好的压电性能和热电性能[10]；王朝辉对电气石改性沥青混合料的路用性能进行了研究，表明电气石对沥青混合料各项路用性能均有不同程度的提高[1112]。……