陈文龙

摘 要：为了得到性能优良的改性乳化沥青，提升改性乳化沥青混合料路用性能，研究了乳化剂复配比例和乳化剂、改性剂以及稳定剂的用量对改性乳化沥青性能的影响，制备出一种高性能乳化沥青，并验证其路用性能。结果表明：乳化剂A与B的复配比例为7∶3、乳化剂用量为25%、改性剂用量为5%、稳定剂用量为08%时，制备的改性乳化沥青各项性能较优；高性能乳化沥青的多项性能均有大幅提升。

关键词：高性能乳化沥青；影响因素；乳化沥青混合料；路用性能

中图分类号：U214.7 文献标志码：B

Research on Influencing Factors of Highperformance Modified Emulsified Asphalt

CHEN Wenlong

（Henan Provincial Institute of Urban and Rural Planning and Design， Zhengzhou 450044， Henan， China）

Abstract： In order to get modified emulsified asphalt with excellent properties and improve the pavement performance of asphalt mixture， the impact of compound proportion of emulsifier and the amounts of emulsifier， modifier and stabilizer on the performance of modified emulsified asphalt was studied. A new type of emulsified asphalt with high performance was presented and the pavement performance of asphalt mixture was confirmed. The results show that with the compound proportion of emulsifier being 7∶3 and the amounts of emulsifier， modifier and stabilizer being 25%， 5% and 08% respectively， the modified emulsified asphalt shows excellent performance， and many properties of the highperformance emulsified asphalt are improved significantly.

Key words： highperformance emulsified asphalt； influencing factor； emulsified asphalt mixture； pavement performance

0 引 言

近年来，乳化沥青因其良好的路用性能被广泛应用于公路建设中，如用作新建道路的透层油或者粘层油，并在微表处、稀浆封层等养护工程以及冷再生沥青混合料中取得了良好的应用效果。孙晓立等分别从微表处以及碎石封层方面对乳化沥青在公路工程养护中的应用进行了研究[12]；张兰峰等研究了乳化沥青在冷再生混合料中的应用[34]。随着现代交通的发展，公路工程建设对改性乳化沥青的性能提出了更高的要求，要求其不仅要具备良好的高低温性能，还要有优良的耐疲劳以及抗水损害性能。为了进一步拓宽乳化沥青的应用范围，制备出高性能改性乳化沥青已成为道路工作者的重点研究内容[57]。本文研究不同影响因素对高性能改性乳化沥青性能的影响，提出一种高性能改性乳化沥青配方，并对其性能进行验证。

1 改性乳化沥青的制备