王然+谢维斌+蒋硕萌+李仕林+胡艳丽

摘要：使用棉、阻燃棉、涤纶、阻燃涤纶织物，研究了采用格栅与否两种情况对锥型量热仪最大热释放速率测试的影响。实验表明，采用格栅后，纯棉、阻燃棉织物最大热释放速率测试值变异系数分别由8.5%、11.1%降至4.6%、4.3%，涤纶、阻燃涤纶织物最大热释放速率测试值由非正态分布转变为正态分布，增加格栅后涤纶、阻燃涤纶织物最大热释放速率测试值变异系数分别为7.2%、8.9%。说明格栅的采用能够显著提高棉、阻燃棉、涤纶和阻燃涤纶织物最大热释放速率测试的重复性。

关键词：棉；涤纶；阻燃；锥型量热仪；变异系数

中图分类号：TS 101.9 文献标志码：A

Influence of Grid on pkHRR Test of CONE

Abstract： The influence of grid on the peak of Heat Release Rate （pkHRR） test of CONE was investigated， in which， cotton， flame-retardant cotton， PET and flame-retardant PET fabrics were used. The test results show that by using grid the coefficients of variation （C.V.） of pkHRR values of cotton and flame-retardant fabrics were reduced from 8.5% and 11.1% to 4.6% and 4.3% respectively， and the pkHRR values of PET and flame-retardant PET fabrics turned from abnormal distribution to normal distribution； and after increasing the number of grid， the C.V. of pkHRR values of PET and flame-retardant PET fabrics stood at 7.2% and 8.9% respectively. This demonstrates that the adoption of grid can significantly increase the repeatability of pkHRR values of these fabrics.

Key words： cotton； PET； flame-retardant； CONE； coefficient of variation

锥形量热仪是一种以氧消耗原理为基础的新一代聚合物材料燃烧测定仪。氧消耗原理是指对于大量的有机气体、液体和固体，完全燃烧消耗单位质量的氧气后所释放的净热量基本是一个常数13.1 kJ/g（±5%）。1982年美国国家标准与技术研究院根据这一原理研制出了新型量热仪，因其辐照加热器为锥形故得名锥形量热仪。与现行其它主要测试方法相比，锥形量热仪的燃烧环境极相似于真实的燃烧环境，其试验结果与大型燃烧试验结果之间存在很好的相关性，可很好地分析材料燃烧性能并估计其在真实火灾中的危险性，在评价材料、材料设计和火灾预防等方面具有重要的参考价值，因此锥形量热仪已经成为研究材料燃烧性能最重要的实验仪器之一。

锥形量热仪测试对象主要集中在厚度 6 mm以上、燃烧时间达数分钟的材料。……