沈忱

摘要：近年来，在吴江地区商品房开发及拆迁安置房的大量建设中，加气混凝土砌块等新型墙体材料正替代着传统粘土砖成为主要绿色建筑材料，但由于其本身的特性，由其砌筑的墙体发生较多的开裂现象，并成为投诉集中点。针对这一问题，重点阐述了加气混凝土砌块墙体裂缝机理，并提出了一系列行之有效的防治措施。

关键词：加气混凝土砌块 开裂 防治

Abstract: In recent years, under the large construction of the real estate development and housing demolition resettlement in the Wujiang area, the aerated concrete blocks and other new wall materials are becoming the main green building materials, which replace the traditional clay brick, but due to its own characteristics, the masonry wall often occurres the cracking phenomenon, it becomes the lodged focus points. To solve this problem, this paper elaborates with emphasis the aerated concrete block wall crack mechanism, and puts forward a series of effective prevention and control measures.

Keywords: aerated concrete block ;crack ;prevention

中圖分类号：TU377文献标识码：A 文章编号：2095-2104（2012）

1.概述

随着建筑行业的蓬勃发展和社会环保意识的不断加强，越来越多的新型环保建筑材料出现在建设领域，加气混凝土砌块等新型墙体材料正替代着传统粘土砖成为主要绿色建筑材料。但是，据建筑行业普遍反映，加气混凝土砌块较传统红砖而言，使用后更容易遇到墙体开裂、渗水，抹灰脱落从而污染、损坏室内装修等问题。实际上，墙体出现裂漏的根本原因并不是因为使用了蒸压加气混凝土砌块，而多是由于把新墙材错误地理解成是一种比红砖轻的“轻质砖”，按照使用红砖的方法来管理和砌筑，而没有按照新工艺进行施工。

要区分新材料与传统材料的施工工艺，首先我们需要了解它们之间特性的不同。蒸压加气混凝土砌块属于硅酸盐制品，因此，它们的物理特性和化学特性与红砖有着本质上的区别：

1.1干燥收缩值

红砖的干缩值一般在0.1mm/m以下，对蒸压加气混凝土砌块，它的干缩值一般为红砖的3～6倍。若要将它的实际干缩值控制在0.1mm/m，则它的相应含水率应在9.8～13.6％之间。……