张平

摘要：大量的工程实践和理论分析表明,钢筋混凝土构件基本上都是带裂缝工作的,只是有些裂缝很细,甚至肉眼看不见(缝宽<0.5ｍｍ),一般对结构的使用无大的危害,允许其存在。有些裂缝在使用荷载或外界物理及化学因素作用下,不断产生和发展引起混凝土碳化、保护层剥落及钢筋锈蚀,使钢筋混凝土强度和刚度受到削弱,耐久性降低,严重时甚至发生垮塌事故,危害结构的正常使用,必须加以控制, 因此研究商品混凝土裂缝产生的原因及预防措施是非常重要而迫切的。 关键词：混凝土结构；裂缝；防治

Abstract: The large number of engineering practice and theoretical analysis shows that the reinforced concrete structures are basically with the cracks to work, but some cracks, very small, even invisible to the naked eye (slit width <0.5mm), the general use of the structure without great harm, allowing it to exist. Some cracks under the load or external physical and chemical factors, the continuous generation and development caused by the carbonation of concrete protective layer spalling and reinforcement corrosion, strength and stiffness of reinforced concrete has been weakened, and durability reduce serious or even collapse accident hazards the normal use of the structure, must be controlled, so research the causes and preventive measures of commodity concrete cracks is very important and urgent.

Key words: concrete structure; cracks; prevention

中图分类号: TU37 文献标识码：A文章编号：

前 言

大量的工程和实践理论分析表明,钢筋混凝土构件基本上都是带裂缝工作的,只是有些裂缝很细,甚至肉眼看不见(缝宽<0.5ｍｍ),一般对结构的使用无大的危害,允许其存在。有些裂缝在使用荷载或外界物理及化学因素作用下,不断产生和发展引起混凝土碳化、保护层剥落及钢筋锈蚀,使钢筋混凝土强度和刚度受到削弱,耐久性降低,严重时甚至发生垮塌事故,危害结构的正常使用,必须加以控制, 因此研究商品混凝土裂缝产生的原因及预防措施是非常重要而迫切的。

一、混凝土裂缝类型及成因

实际上,钢筋混凝土结构裂缝的成因复杂而繁多,甚至多种因素互相影响,但每一条裂缝均有其产生的一种或几种原因，其中最常见的是混凝土早期裂缝，混凝土早期裂缝有以下几种：

1、塑性沉降裂缝

此类裂缝产生的主要原因是由于混凝土骨料沉降时受到阻碍（如钢筋、模板）而产生的。这种裂缝大多出现在混凝土浇注后0.5小时至３小时之间，混凝土尚处在塑性状态，混凝土表面消失水光时立即产生，沿着梁及板上面钢筋的走向出现，主要是混凝土塌落度大、沉陷过高所致。另外在施工过程中如果模板绑扎的不好、模板沉陷、移动时也会出现此类裂缝。

2、塑性收缩裂缝

此类裂缝产生的主要原因是混凝土浇筑后，在塑性状态时表面水分蒸发过快造成的。这类裂缝多在表面出现，形状不规则、长短宽窄不一、呈龟裂状，深度一般不超过50mm。产生的原因主要是混凝土浇注后３—４小时左右表面没有被覆盖，特别是平板结构在炎热或大风天气混凝土表面水分蒸发过快，或者是基础、模板吸水过快，以及混凝土本身的水化热高等原因造成混凝土产生急剧收缩，此时混凝土强度趋近于零，不能抵抗这种变形应力而导致开裂。……