赵东江，马松艳

（绥化学院 生物与食品工程系，黑龙江 绥化 152061）

（Departmentof Biologic and Food Engineering,Suihua University,Suihua 152061，China）

环境工程

采用湿法技术从废旧锂离子电池中回收有价金属*

赵东江，马松艳

（绥化学院 生物与食品工程系，黑龙江 绥化 152061）

采取湿法回收技术对废旧锂离子电池进行处理，研究了回收铝、钴、锂金属元素的工艺条件。在90℃时，用10%NaOH浸出铝，其浸出率达到96%。在温度90℃、4mol·L-1H2SO4、固-液比1∶8、反应时间100min的浸出条件下，钴、锂浸出率为92%。利用NaHCO3和Na2CO3为沉淀剂，从酸浸出液分别制备得到CoCO3和Li2CO3产品。

废旧锂离子电池；浸取；回收；有价金属

（Departmentof Biologic and Food Engineering,Suihua University,Suihua 152061，China）

Abstract:The spent lithium-ion batteries were treated by using hydrometallurgy technology and the process conditions of the recovery of aluminum,cobalt and lithium metallic elements were studied.The leaching ratio of aluminum element reached 96%in 10%NaOH solution at 90℃.As the leaching conditions are temperature 90℃,4mol·L-1H2SO4,solid-liquid ratio 1∶8 and reaction time 100min,the leaching ratio of cobalt and lithium is 92%.The CoCO3and Li2CO3products were obtained from the acid-leaching solution using NaHCO3and Na2CO3for precipitation agent,respectively.

Key words:spent lithium-ion batteries;leaching;recycling;valuablemetals

随着电池产销量的逐年增长，废旧电池的回收和处理引起人们的极大关注。比如，利用废旧锌锰电池可以回收锰、锌等金属，不但减少了废旧电池对环境的污染，而且可以实现锌、锰等金属资源再生利用[1,2]。锂离子电池广泛应用在电动汽车、航天以及小型移动电子设备等领域[3,4]，其平均寿命在500～1000次循环，使用时间为3年左右，因此，废旧锂离子电池回收处理问题同样受到了普遍重视[5-7]。文献报道[8]，一支重约40g的手机锂离子电池，钴、铜、铝、铁、锂等金属含量分别为15%、14%、4.7%、25%和0.1%，对其回收处理可以实现资源综合利用，变废为宝。目前，废旧锂离子电池回收处理技术主要分为火法处理和湿法处理两种，湿法冶金技术具有对环境污染小的优点，已被国内外研究者广泛采用[9]。本文利用湿法处理技术，采取碱浸-酸溶的方法对废旧锂离子电池正极材料进行处理，研究了回收钴、铝、锂金属元素的工艺条件，制备得到氢氧化铝、碳酸钴、碳酸锂等化合物。……