摘要：大体积混凝土应用技术一直是建设工程领域关注的焦点，具有混凝土一次性浇筑量大、胶凝材料水化热散发难、临时施工设施复杂、质量控制点多、技术含量高等特点。如施工质量控制不当，易出现混凝土开裂、地下室底板或外墙渗水等问题。作者结合相关理论研究及工程实践经验，给出了具体的技术措施，以供参考。

关键词：大体积混凝土;质量控制;技术措施

Abstract： The application technology of mass concrete has always been the focus in the field of construction engineering，it is characterized by large quantity of concrete pouring in one time，difficult to dissipate hydration heat of cementitious materials，complicated temporary construction facilities，many quality control points and high technical content.Such as construction quality control is not appropriate，easy to appear concrete cracking，basement floor or wall seepage and other issues.Combined with relevant theoretical research and engineering practice experience，the author gives specific technical measures for reference.

Keywords： mass concrete; Construction quality control; Technical measures

0 引言

大體积混凝土指结构实物最小尺寸≥1m或预计会因胶凝材料水化引起的温度变化和收缩导致有害裂缝产生的混凝土。原材料和配合比参数选用不当、施工管理不到位、温控措施不合理等均可导致大体积混凝土出现裂缝。

1理论研究

大体积混凝土除水泥、砂、石、水四种原料外，还需要掺加矿物掺合料和多种外加剂，由此增加了管理和施工难度。工程实践中，除需按GB50496[1]进行温度应力验算外，还可从以下几个方面加以防控：

1.1原材料选择及配合比设计

选用低水化热水泥，如粉煤灰或矿渣硅酸盐水泥等。不宜选用通过增加比表面积来提高早期强度的水泥，避免使用超过60℃的“新鲜”水泥。

选用非碱活性的粗骨料，如使用了无法判定是否是碱活性骨料或有碱活性的骨料时，可选用GB175[2]规定的低碱水泥。

矿渣可替代水泥-粉煤灰复合胶凝体系中的水泥，但不能替代粉煤灰。GB/T 50146[3]提供了掺合料取代水泥的最大限量。

外加剂使用前应进行其与水泥的适配性试验，超长大体积混凝土跳仓法施工中不应使用膨胀剂或膨胀型外加剂。……