张鸿朋 马芹永

摘 要：通过自密实性能试验和早期拉压强度试验，研究不同体积掺量的玄武岩纤维、聚丙烯腈纤维以及玄武岩-聚丙烯腈混杂纤维对自密实混凝土的流动性、间隙通过性以及7d劈裂抗拉强度和立方体抗压强度的影响。试验结果表明，随着纤维掺量的增加，自密实混凝土的流动性和间隙通过性会逐渐降低;混杂纤维对自密实混凝土抗拉强度的提升效果较抗压强度更为显著，当玄武岩纤维和聚丙烯腈纤维的掺量分别为0.20%和0.12%时，劈裂抗拉强度的增幅最大，较素自密实混凝土提高了87.5%。

关键词：玄武岩纤维;聚丙烯腈纤维;自密实性能试验;劈裂抗拉强度;抗压强度

Abstract：The effects of basalt fiber， polyacrylonitrile fiber and basalt-polyacrylonitrile hybrid fiber with different volume contents on the fluidity， permeability， 7d splitting tensile strength and cubic compressive strength of self-compacting concrete were studied through the self-compacting performance test and early tension-compression strength test. The results show that the fluidity and clearance passability of self-compacting concrete will decrease with the increase of fiber content. When the contents of basalt fiber and polyacrylonitrile fiber are respectively 0.20% and 0.12%， the splitting tensile strength of self-compacting concrete increases the most， 87.5% higher than that of plain self-compacting concrete.

Key words：basalt fiber; polyacrylonitrile fiber; self-compacting performance test; splitting tensile strength; compressive strength

随着我国建设单位对工程进度、质量及成本的要求不断提高，人们也对周围的生活环境有了更高的追求，因此实际工程中自密实混凝土成为了更好的选择[1-3]。然而在自密实混凝土制备过程中胶凝材料和水的用量大，极易出现早期收缩开裂，裂缝的产生会影响结构的承载力[4-6]，而纤维的掺入可以增强与混凝土之间的粘结力，从而提高结构的强度。但是自密实混凝土的流动性会随着纖维掺量的增加而下降。因此，在自密实混凝土中掺纤维并找到纤维掺量的合理配比区间就显得尤为重要[7-8]359。

文献[9]在普通混凝土试件中掺入不同掺量的玄武岩-聚丙烯腈混杂纤维，发现纤维的掺入可以大幅提升混凝土的劈裂抗拉强度，但在一定程度上降低了混凝土的抗压强度。……