旃开发　刘浩蔷　闵小林　马露雪　刘荥　郭启龙

摘  要：文章针对机制砂中石粉含量对混凝土性能的影响，结合具体实验数据探究了机制砂、粉煤灰和石粉含量对混凝土性能的影响;结果表明，随着机制砂含量的增加，坍落度不斷降低，抗压强度先增加后降低，当含量为40%时，抗压强度达到最大值。粉煤灰的适量掺入可以改善混凝土的工作性能，掺量为20%时提高了混凝土的抗压强度。适量的石粉可以改善混凝土的工作性能，提高其抗压强度，当石粉含量高于13%，降低混凝土工作性能和抗压强度。因此，当机制砂掺入为40%，粉煤灰为20%和石粉含量为13%时，C30混凝土的抗压强度最高。

关键词：机制砂;石粉;河砂;粉煤灰;混凝土

中图分类号：TU528         文献标志码：A         文章编号：2095-2945（2020）08-0051-04

Abstract： Aiming at the effect of the stone dust contenton the concrete performance in the manufactured sand， this paper explores the effect of the manufactured sand， fly ash and stone dust contenton the concrete performance with specific experimental data; the results show that with the increase of the content of the machine sand， the slump continues to decrease， and the compressive strength increases first and then decreases. When the content is 40%， the compressive strength reaches a maximum.An appropriate amount of fly ash can improve the workability of concrete， and the compressive strength of concrete is increased when the amount is 20%.A proper amount of stone powder can improve the workability and compressive strength of concrete. When the content of stone powder is higher than 13%， the workability and compressive strength of concrete are reduced.Therefore， when the incorporation of machine sand is 40%， fly ash is 20% and stone dust contentis 13%， the compressive strength of C30 concrete is the highest.

Keywords： manufactured sand; stone powder; river sand; fly ash; concrete

1 概述

我国持续推进经济建设，随着建筑行业高速发展，建筑用砂需求逐渐增大，天然河砂大量开采，国内大部分地区资源匮乏，生态遭到严重破坏，受到国家高度重视，为杜绝该类问题产生，《森林法》第十三条规定，禁止采天然砂等毁坏生态行为，所以市面上天然砂资源匮乏。国家在两会上也明确指出，倡导发展机制砂产业，进行生态文明建设，大力推进机制砂代替河砂，为响应国家号召，机制砂取代河沙已经逐渐应用在工程实践中。

机制砂是由石头破碎而成的直径小于4.75mm的岩石颗粒。它具有多棱角、级配不良等特点。在混凝土中，它可以增加彼此之间的咬合力，提高混凝土强度[1]，机械破碎而成的机制砂还含有一定量的石粉（粒径小于75？……