邓玮玮 刘德玉 许文年

摘要：以植被混凝土生态基材为研究对象，探讨了植生土类型和初始含水率两个因素对其在冻融过程中水分迁移的影响。通过试验对冻融过程中进行温度场以及冻融前后含水量的变化进行分析。研究结果表明：植被混凝土中的水完全冻结的时间受初始含水率和植生土类型的影响，初始含水率越大，冻结到底所需的时间越长;土样冻结后在试样顶部会出现含水量明显增大的土层，初始含水率越大，水分聚集的越多。

Abstract： Taking the vegetation concrete ecological substrate as the research object， the effects of planting soil type and initial moisture content on water migration during freezing and thawing were discussed. The temperature field during the freeze-thaw process and the change of water content before and after freezing and thawing were analyzed by experiments. The results show that the time of complete freezing of water in vegetation concrete is affected by the initial water content and the type of planting soil. The larger the initial water content， the longer the time required for freezing. After the soil sample is frozen， there will be a soil layer with a significant increase in water content at the top of the sample.The greater the initial moisture content， the more water is accumulated.

關键词：植被混凝土;温度场;含水率;水分迁移

Key words： vegetation concrete;temperature field;water content;water migration

中图分类号：TU411                                      文献标识码：A                                  文章编号：1006-4311（2019）26-0285-03

0  引言

植被混凝土生态防护技术[1]自成功发明以来，受到广泛认可和应用。该技术应用的大部分区域为华南、华中等地区，这些地区的气温条件一般较高，一般不会发生冻融现象，生态修复与边坡防护功能也不会受较大影响。但是目前有许多西部高寒地区边坡裸露工程急需修复，高寒地区气候条件较为恶劣，常年处于低温状态。在这种温度条件下，土中的水分会冻结成冰，形成冰晶体，产生冻胀现象，而当温度高于冻结温度的时候，冰晶体会融化成水，会造成融沉现象，由于多次的冻融循环，土体内部结构遭受破坏，土体就会坍塌和破坏。植被混凝土生态防护技术是将人工生态基材喷射到边坡的表层，基材中也不可避免的含有水分，从而也会受到冻融现象的影响，这也是目前该技术在高寒地区工程建设中面临的主要问题，严重影响生态恢复的质量和经济效益，为此，研究植被混凝土生态基材冻融过程中水分的迁移情况十分必要。……