【摘 要】笔者根据多年的工作经验，并结合具体工程实例阐述了高层建筑混凝土施工技术的特性，提出不能将一般的混凝土施工工艺套用在高层建筑上施工，为解决混凝土施工中强调的问题，提供施工指导借鉴。以下也只是笔者在实践工作中对问题一些浅薄的认识。以供同行参考！

【关键词】高层建筑;混凝土施工;特性

On the concrete high-rise building construction technology

Huo Hai-kuan

（Shanxi Fenxi Construction Company LLC Jian Jiexiu Shanxi 032000）

【Abstract】Based on years of experience， combined with specific examples of projects elaborated characteristics of concrete high-rise building construction technology， construction technology generally made of concrete can not be applied in the construction of high-rise buildings， to address the issues highlighted in concrete construction， construction guidance provided for reference . The following are just my work in practice some of the shallow understanding of the problem. For peer reference！

【Key words】High-rise buildings;Concrete construction;Characteristics

1. 工程实例

某大厦有2栋28层的高级商品办公住宅楼组成，±0.00以上设四层裙楼，二座塔楼，地下室二层，总高度为84.60m，建筑物结构类型为钢筋砼框剪结构，基础采用人工挖孔桩，主楼钢筋混凝土筏形基础承台板厚3.00m，平面45.2m×45.2m，承台混凝土量为6129.12m3。地下车库承台板厚1.00m，混凝土量为2426m3，承台混凝土强度等级为C45，抗渗等级S6。

1.1 选择砼原材料。

为保证大体积砼的施工质量，原材料的选择极为重要，对进场材料要选择，符合各项规范要求方可使用。水泥：选用525#普通硅酸盐水泥并适当掺加粉煤灰。根据大体积砼的特点，砼的强度等级一般为高标号砼，为了降低水泥的水化热，在满足砼质量要求的条件下，适当外掺粉煤灰，同时还可以减少水泥用量，并延迟水化热高峰期的到来，有利于砼的强度增长，避免温度应力过大而产生裂缝。碎石：选用级配较好的花岗岩碎石，粒径为10～30mm，含泥量不得大于1%，且不得含有有机杂质。砂：选用级配较好的中粗砂，含泥量不得超过2%，通过0.315mm 筛孔的砂不得少于15%。外加剂：选用具有缓凝系减水剂和膨胀剂，从而降低水灰比。

1.2 混凝土施工方案。……