赖辉

【摘 要】根据乳化沥青冷再生混合料强度形成机理，提出乳化沥青冷再生混合料配合比设计方法，并针对乳化沥青冷再生混合料的和易性和早期强度两项关键指标进行了详细的介绍，提出了乳化沥青冷再生混合料和易性评价方法及早期强度的保证措施。同时，结合工程实践提出了乳化沥青冷再生路面施工质量影响的主要因素及其控制指标和参数。论文对于乳化沥青冷再生混合料配合比设计及相关工程实践具有重要参考价值。

【关键词】冷再生;乳化沥青;配合比设计;和易性;早期强度

Design and performance evaluation method of emulsified asphalt cold recycled mixture

Lai Hui

（Chongqing Municipal Design and Research Institute Chongqing 400000）

【Abstract】According to the formation mechanism of emulsified asphalt cold recycled mixture， the design method of emulsified asphalt cold recycled mixture was proposed. The key indicators of workability and early strength of emulsified asphalt cold recycled mixture were introduced in detail. Evaluating method for the evaluation of the ease of emulsified asphalt cold recycled mixture and early strength. At the same time， combined with engineering practice， the main factors and control indexes and parameters of the construction quality of emulsified asphalt cold recycled pavement were proposed. The paper has important reference value for the mix design of emulsified asphalt cold recycled mixture and related engineering practice.

【Key words】Cold regeneration;Emulsified asphalt;Mix design;Workability;Early strength

1. 引言

（1）自2003年第一条乳化沥青冷再生在沪宁高速上的应用开始，乳化沥青冷再生变逐渐在一些省份开始进行一些试验性的研究和试验段的铺筑，在江西九景高速、昌九高速甚至得到了大规模的应用，虽然从当时的情况来看，取得了一定的突破，但在实施过程中仍然存在许多问题，如混合料得不到良好的裹覆、路面成型慢等。造成这些问题的根本原因在于对乳化沥青冷再生混合料的组成设计与性能评价方面的认识存在不足，有待进一步研究。

（2）乳化沥青冷再生混合料组成包括乳化沥青、旧沥青、集料、水泥，乳化沥青中又包含乳化剂、水和基质沥青，其组成成分相对普通的热拌沥青混合料复杂。由于冷再生混合料中一般都含有水分，冷再生混合料的配合比设计和半刚性材料的配合比设计也存在相似之处。因此很多学者在进行乳化沥青冷再生混合料设计时，最佳含水量按照半刚性基层的土工击实试验来确定，混合料的级配合成、最佳乳化沥青用量、以及混合料的最终性能验证过程则跟热拌混合料比较相似。……