摘 要：近年来，我国工业领域发展速度较快，因此对锅炉的运行要求也逐步提升。但目前，锅炉压力管道在运行时仍存在较多缺陷，并且以裂纹缺陷最为突出。常见的裂纹可分为疲劳、腐蚀、焊接等多种不同的类型，会严重影响管道运行质量。基于此，本文提出切实可行的预防裂纹产生的措施。

关键词：锅炉；压力管道；裂纹

中图分类号：TK228 文献标识码：A 文章编号：1003-5168（2018）13-0031-02

Analysis of Crack Problem and Preventive Treatment

Method in Boiler Pressure Pipeline Inspection

LIN Cunzhong

（Quanzhou Branch of Fujian Boiler and Pressure Vessel Inspection and Research Institute，Quanzhou Fujian 362000）

Abstract： In recent years， China's industrial sector has developed rapidly， so the requirements for the operation of boilers have been gradually improved. However， at present， there are still many defects in the operation of boiler pressure piping， and crack defects are most prominent. Common cracks can be divided into different types， such as fatigue， corrosion， welding and so on， which will seriously affect the quality of pipeline operation. Based on this， this paper put forward feasible measures to prevent cracks.

Keywords： boilers； a pressure pipe；a crack

鍋炉压力管道的运行环境极其复杂，不仅长期处于高温状态下，而且需要承受过大的压力，因此容易出现裂纹。裂纹缺陷不仅会影响管道质量，而且会危及设备及操作人员的生命安全，还会严重影响企业的运营和经济效益，因此，必须加强对管道的定期检验和经常性的安全检查，定期监测管道动态，并对检验数据和检查结果进行分析，进而了解裂纹的特点并加以控制。同时，还应在施工前对原材料进行检验，从源头上控制裂纹问题。本文主要分析锅炉压力管道检验中的裂纹问题及预防措施。

1 常见裂纹及原因

1.1 疲劳裂纹

疲劳裂纹包括多种类型。第一种是机械疲劳裂纹，该类裂纹发生的部位主要包括叶轮和叶片等，其与腐蚀介质关联性较强。另外，材料质量及环境因素会导致裂纹程度加深。可见，该类裂纹的分析过程较为复杂，涉及因素较多，需要进行综合性考量[1]。第二种是热疲劳，其是在热交变应力的影响下产生的，多发生在疏水管座及排气管座等部位。如果该类裂纹未能得到及时控制，则会导致相关部件二次开裂，且整个变化过程没有任何规律，随意性较强[2]。……