【摘 要】用于防止发电厂炉膛水冷壁发生高温腐蚀而加装炉膛贴壁风系统，由于对二次风造成分流作用，使得侧墙氧量增加，大大破坏原先的内部流场分布，在减少侧墙水冷壁发生高温腐蚀的同时，造成屏过、高过管壁温度极易发生超温状况。由于炉膛贴壁风的介入，同时针对各产地的差异煤种，锅炉各配风风量，总煤粉量、總风量等锅炉参数必须做出相应的改变调整才能保证燃煤的快速着火和燃尽。

【关键词】贴壁风；高温腐蚀；超温；控制措施

中图分类号： TG142.71 文献标识码： A 文章编号： 2095-2457（2018）12-0033-002

DOI：10.19694/j.cnki.issn2095-2457.2018.12.014

【Abstract】to prevent power plant furnace water wall high temperature corrosion and equipped with a stove or furnace wall wind system， due to the secondary air distribution function， increase oxygen side walls， greatly damage the original internal flow field distribution， side to reduce high temperature corrosion of water wall occurred at the same time， due to screen， above overtemperature tube wall temperature easily happened. Because of the furnace wall wind intervention， at the same time， in view of the different types of the origin， boiler air distribution air volume， total amount of pulverized coal， total air volume must make the corresponding adjustment to change the boiler parameters， such as to ensure fast ignition and burning of coal.

【Key words】Wall sticking wind； High temperature corrosion； Overtemperature； Control measures

0 引言

在如今国内电厂新环境之下，大容量锅炉使用趋于常态，与此同时，伴随的是超超临界锅炉的高热负荷；热值低，灰份高的燃煤使用，造成电厂锅炉不同程度，不同形式的高温热腐蚀，而经过多方论证，实践，炉膛加装贴壁风来解决水冷壁侧墙高温腐蚀的技术已经逐渐成熟而广泛应用，在提高锅炉安全运行系数的同时，贴壁风加装是一项系统简单，投入小且冷却效果明显的方案。但是，后加装的系统总会与之前的结构在稳定运行及调整方面上有着明显的不相容，产生别的问题，对于本厂1000MW的锅炉加装炉膛贴壁风之后，屏过，甚至是高过的超温现象频频发生，同时也伴随着其独有的特点威胁着锅炉的正常稳定运行，因此，针对这种情况，从结构现象出发，并对引发的原因深入分析研究，从而提出有效的调节思路和控制方法，以保证机组的高效稳定可控运行。……