【摘 要】多层共挤聚烯烃热收缩膜（POF）是近年来出现的新型热收缩包装材料。而设备中关键部件“多層共挤装置”（模头）的结构将直接影响着产品的生产质量。本文通过对传统模头的改进，在模口的圆周上增加36个螺纹孔，以利用螺钉进行对模口的微调，从而提高POF膜管厚度的均匀性，改善了产品的生产质量。

【关键词】POF；三层共挤；吹塑机；模头；微调

中图分类号： TQ320.52；TP183 文献标识码： A 文章编号： 2095-2457（2018）03-0236-003

Improvement of Multilayer Coextrusion Blow Molding Machine Die

TANG Ben-zhou

（Guangdong Yuedong Advanced Technical School， Shantou Guangdong 515000， China）

【Abstract】Multi-layer co-extruded polyolefin heat shrinkable film （POF） is a new type of heat shrinkable packaging material appearing in recent years. The key component of the equipment， “multi-layer co-extrusion device” （die） structure will directly affect the quality of the production of the product. In this paper， through the improvement of the traditional die， 36 threaded holes are added on the circumference of the die to make fine adjustment of the die using screws， so as to improve the thickness uniformity of the POF film tube and improve the production quality of the product.

【Key words】POF； Three-layer coextrusion； Blow molding machine； Die； Fine-tuning

0 前言

多层共挤聚烯烃热收缩膜（POF）是近年来出现的新型热收缩包装材料，是一种环保型包装材料。塑料挤出成型是塑料制品的主要加工方法之一，它是通过挤出机的加热和混炼使固态原料变成均匀的粘性流体，即在专用设备中将线性低密度聚乙烯（LLDPE）作为中间层，聚丙烯（PP）作为内、外层，经特殊工艺将内、中、外三层共同挤压，在挤压系统的作用下，以一定的压力和速度连续地通过机头而获得一定的形状，从而制成的具有高透明度、高收缩率及热封性能良好的热收缩薄膜。

但在生产过程中怎么保证薄膜厚薄均匀度，是生产过程中最难解决的问题之一。某热收缩膜有限公司的设备所生产出的薄膜就出现厚度不均匀的现象。因质量上出现问题，导致许多客户的流失，严重影响企业的经营发展。

笔者参与了对该设备的改进工作，对生产中遇到薄膜厚度出现不均匀的问题作出分析与调试，最后解决了这一生产难题。

1 准备工作

在参与此次工作前，为了慎重及少走弯路，在开始解决问题之前，我查找了有关资料，进一步分析了该设备的结构原理、生产工艺及其它各种条件，以防盲目的开展此次工作，造成不良后果。……