□ 蔡礼君

青瓷釉色的成因及相关的鉴定原理

□ 蔡礼君

Ferrous oxide and the following secondary oxidation atmosphere formed by “chemical color”, the other is split phase structure in the isolated phase particles into blue half wave scattering formed in the range of “physical color”. The early celadon with chemical color is given priority to, in the late physical color is given priority to. Secondary oxidation feature provides a method of treasure of ancient ceramics authenticity; According to the correlation between chemical composition and smaller “powder blue glaze, can discern the celadons. Secondary open patches of grain width of microscopic differences is another effective way to identification of ancient ceramics.

一、早期青瓷釉色的化学特征

1.现在看到的早期青瓷的釉色

东汉青瓷和春秋至西汉原始瓷相比有了重大进步。吸水率只有0.3%,烧成温度约为 1260 -1310℃。东汉青瓷的产地主要在浙江宁绍平原、金华丘陵和永嘉沿海地区。而北方则是从北魏时起,黄堡镇瓷器就已具规模。这些早期青瓷瓷土含铁量比较高，采用石灰釉,釉料中含氧化钙达15%以上，釉层较薄。由图1-4可见，我们现在看到的早期青瓷无论是南方越窑还是北方的耀州窑的釉色均偏棕绿和棕黄(图1-4）。

晚唐诗人陆龟蒙曾经描述当时的越窑瓷器：“九秋风露越窑开，夺得千峰翠色来”，何为“千峰翠色”？因为诗人是南方人，字面意义应该是越窑釉色就像覆盖山岚的郁郁葱葱的翠色（深绿）。可是为什么我们在现在的越窑藏品上又看不到这样的“翠色”，或者说与那样美丽的“翠色”不相符呢？

2.早期青瓷出窑时的颜色是“翠色”

颜色可以分为“化学色”、“物理色”两种。“化学色”是物质的本色。不同的物质对白光照射后有不同的反射：白光包含七色可见光，物质颜色是反射出来的那部分色光，其他部分色光被吸收。“物理色”则不同，它不是反射色光，而是物质微粒对白光的散射形成的。最简单的例子，就是天空的蓝色不是空气的反射“化学色”而是空气微粒对日光的“瑞利散射”的“物理色”。早期青瓷是化学色还是物理色？因为早期青瓷釉层很薄、温度也较高，没有证据证明釉层中存在明显的分相结构层（例如胶体结构层），显示不出瑞利散射的乳浊的“蓝色”①②③。……