贾慧玲 祁峰　刘崭

摘 要：为了对比目前国内应用最广泛的两类温拌剂对沥青混合料性能的影响，从温拌机理出发，对添加了乳化类温拌剂和有机类温拌剂的沥青混合料进行不同温度下的马歇尔试验和路用性能试验，并对比分析试验结果。研究表明：击实温度降低20 ℃时，有机类温拌沥青混合料的车辙动稳定度有显著提高，水稳性和低温弯曲应变略有降低，其他性能指标均与热拌沥青混合料相当；击实温度降低40 ℃时，部分指标不能满足规范要求。

关键词：道路工程；温拌沥青；成型温度；路用性能

中图分类号：U414 文献标志码：B

Study on Effect of Performance of Warm Mix Asphalt

JIA Huiling1， QI Feng2， LIU Zhan2

（1. Xianyang Management Department of Municipal Engineering， Xianyang 712000， Shaanxi， China；

2. Xian Highway Institute， Xian 710065， Shaanxi， China）

Abstract： In order to study the effect of two most widely used warm mix agents on the performance of asphalt mixture， Marshall test and pavement performance test were conducted at different temperatures on asphalt mixtures adding emulsified warm mix agent and organic warm mix agent， and the comparison was carried out. The results show that when the compaction temperature drops by 20 ℃， the dynamic stability of asphalt mixture with organic warm mix agent increases significantly， while water stability and low temperature bending strain diminish a bit； when the compaction temperature drops by 40 ℃， some indicators do not meet the specification requirements.

Key words： road engineering； warm mix asphalt； forming temperature； pavement performance

0 引 言

温拌沥青混合料与传统的热拌沥青混合料相比，其拌和与压实温度相对较低，可减少能源的消耗和废气的排放，并具有较好的路用性能，是一种新型的节能环保型道路材料，已得到大力推广[13]。目前，在中国应用最广泛的2种温拌技术是有机添加剂法和表面活性剂法；然而，由于缺乏统一的设计规范与标准，以及不同类型的温拌剂作用机理不同，导致其对沥青混合料的降温幅度存在差异，因此在温拌沥青混合料的实际应用过程中，不可避免地碰到了一些问题[46]。

本文通过室内试验对采用以上2种温拌技术制备的温拌沥青混合料的性能进行全面对比分析，为其在工程中的应用提供技术支撑。

1 温拌机理

温拌技术最根本的原理是通过降低沥青粘度或提高混合料工作性能达到降低沥青混合料各环节施工温度的目的，同时保证路面的压实度[78]。……