发泡剂对PVC木塑复合装饰板性能的影响

刘刚连1龚迎春2吴章康1汤正捷1

(1.西南林业大学材料工程学院，云南 昆明 650224，2.中国林业科学研究院木材工业研究所，北京 100091)

摘要：通过测试PVC基木塑装饰板的物理力学性能，研究复合发泡剂配比和发泡剂添加方式对PVC木塑装饰板的密度、抗弯强度、表面结合强度、板面握螺钉力和72h吸水厚度膨胀率的影响。结果表明:添加当复合发泡剂AC、ZnO、NaHCO3配比为6∶1∶4时，PVC木塑复合装饰板的抗弯强度、表面结合强度、板面握螺钉力最大，分别为21.08MPa、0.67MPa、0.82kN，达到GB/T 24137—2009《木塑装饰板》的要求；采用直接添加发泡剂的PVC木塑复合装饰板的力学性能优于采用先混合物料后添加发泡剂的PVC木塑复合装饰板的力学性能。

关键词：木塑装饰板；聚氯乙烯；发泡剂；力学性能

中图分类号：S781.2

文献标志码：A

文章编号：2095-1914(2015)02-0105-05

Abstract:The effects of the ratios and adding ways of foaming agent on the properties of the PVC wood-plastic composite(WPC)decorative boards by testing the physical and mechanical properties. Results showed that，when the ratio of composite foaming agent AC, ZnO, NaHCO3 was 6∶1∶4, the bending strength, the surface bonding strength，and the screw holding capability of WPC decorative boards to maximum were 21.08MPa，0.67MPa，0.82KN，respectively. And then they met the GB/T 24137—2009standards. The mechanical properties of WPC decorative boards with directly adding the composite foaming agent were better than that with first mixing and then adding the foaming agent.

Keywords:wood-plastic composite decorative boards;PVC;foaming agent;mechanical properties

The Effects of the Foaming Agent on Properties of PVC

Wood-Plastic Composite Decorative Boards

LIU Gang-lian1,GONG Ying-chun2,WU Zhang-kang1,TANG Zheng-jie1

(1.College of Materials Engineering, Southwest Forestry University, Kunming Yunnan 650224,China；

2.Research Institute of Wood Industry, Chinese Academy of Forest, Beijing 100091,China)

木塑复合材料(wood-plastic composites，WPC)是一种新型环保材料，以植物的木质粉料或木纤维作为增强填料，经过预处理后与热塑性塑料(1种或多种)混合，同时添加一些其他助剂，经过热压、挤出、注塑等方式加工而成的复合材料[1-3]。木塑复合材料兼备了木材和塑料的双重特性，可加工制成多种颜色 ，其纹理和加工性能与木材相似，同时还具有化学性能稳定、强度高、抗虫菌效果较好、可回收利用等优点，是一种理想的代木材料。优良的综合性能使木塑复合材料有着广泛的应用领域，如家具、包装、汽车、航空、交通运输、体育用品、休闲用品、装饰材料及日常生活用具等[4]。

PVC塑料的密度较大，加工过程中的挤压工艺使木质粉料密实化，制得的木塑复合材料密度较大，通常为1.2～1.4g/cm3，较大的密度使其在室内装饰材料领域受到限制[5-6]。……