【摘要】温再生沥青混合料是一种基于温拌沥青技术的新型再生沥青混合料，实现了旧沥青混合料（RAP）循环利用和节能减排的双重目标。本文通过与热再生沥青混合料的对比试验，研究了不同旧料掺量下温再生沥青混合料的路用性能。结果表明：温再生沥青混合料各项指标均已接近或达到了热再生沥青混合料的性能，而且旧料的掺配率可以提高10%左右；旧料掺量为20～30%时，温再生混合料的性能良好，可用于城市道路沥青路面的建设。

【关键词】温再生沥青混合料；热再生沥青混合料；路用性能；掺量

Abstract：Warm-recycled asphalt mixture is a new type of pavement material that can realize the RAP recycling and energy saving and emission reduction. Trough the comparative test of hot-recycled asphalt mixture， the article studied the comprehensive pavement performance of warm- recycled asphalt mixture with the addition of different reclaimed asphalt pavement（RAP） admixture amount. The results showed that： all indicators of the warm- recycled asphalt mixture were close to or reached the performance of hot-recycled asphalt mixture，and the admixture amount of RAP can be improved about 10%. The RAP content should be among 20～30% when the WMA recycled mixture used in high grade highway construction.

Key Words：warm- recycled asphalt mixture， hot-recycled asphalt mixture，performance evaluation，admixture amount

0引言

随着合肥市经济的快速发展和城市定位的大幅提升，既有的城市道路已经无法满足城市发展的需要。近年来，合肥市对老城区的多条市政道路进行了大规模的改扩建，并通过“畅通一环，打通中环，改造二环”工程的实施，全面提升城市交通服务水平。在城市道路改扩建中，产生了大量的废旧沥青混合料，这些废旧沥青混合料如不加以利用，不仅会造成资源的大量浪费，而且因为需要堆放场地，还会造成空间浪费和环境污染。因此，沥青路面再生技术逐渐引起研究与工程人员的广泛关注。在我国，广泛应用的沥青路面再生技术主要是厂拌冷再生技术 [4]，厂拌热再生混合料具有较好的使用性能良好，但是存在能耗大、污染严重、旧料掺配比例低、成本高等缺点，而温再生沥青混合料技术可以极大地弥补这一缺陷，通过添加合适的温拌剂，可以降低热再生混合料的拌和温度、节能减排、减少沥青及再生剂的老化、提高旧料掺配率，势必带来巨大的社会效益和环境效益[5]。……