秦建等

摘要： 采用焊条电弧焊在0Cr18Ni10Ti奥氏体不锈钢表面堆焊Inconel 625，并对堆焊层的金相组织、化学成分、拉伸性能、弯曲性能及断裂形貌进行了分析测试。试验结果表明：堆焊接头焊缝熔合良好，未出现焊接缺陷；焊接接头抗拉强度达到780 MPa，断裂形式为韧窝状的韧性断裂；弯曲性能能够满足要求；堆焊层显微组织为枝晶状的γ组织；化学成分检测未见异常。

关键词： 0Cr18Ni10Ti； Inconel 625； 焊条电弧焊； 堆焊

中图分类号： TG457

Abstract： Inconel 625 was welded on the surface of 0Cr18Ni10Ti austenitic stainless steel by SMAW. The microstructure，chemical composition， mechanical properties and fracture morphology of the surfacing welded joints were investigated. The results showed that well fusion weld was obtained in this experiment，and there was no weld defects. The welded joint tensile strength reaches 780 MPa which fracture morphology was dimple. The bending performance could meet the requirements. The microstructure of surfacing was dendritic γ . There was no abnormalities detected in chemical composition.

Key words： 0Cr18Ni10Ti； Inconel 625； SMAW； surfacing

0 前 言

换热器作为实现物料之间热量传递过程的设备在石化、炼油、动力等工业部门广泛应用[1]。由于其在服役过程中长期经受高温、高压、酸碱性介质腐蚀，因此其材质往往选用不锈钢材料。随着炼化产品介质及环境的复杂化，传统的不锈钢材质已经不能满足使用要求，镍基耐蚀合金由于其具有优良的耐热和耐蚀性而在石油化工、电力和宇航等行业得到了推广应用[2]。镍基材料价格昂贵，比较经济的方法是在不锈钢内壁堆焊镍基材料以保证设备的抗腐蚀能力，这就涉及到镍基合金和不锈钢异种材料的焊接问题，由于镍基合金本身就具有较高的热裂纹敏感性及较差的液态金属流动性，因此在焊接过程中往往要采用一定的工艺措施来保证焊接的质量[3]。

文中采用手工电弧焊方法在0Cr18Ni10Ti奥氏体不锈钢表面堆焊ENiCrMo3镍基焊材，通过分析堆焊层的显微组织、化学成分和力学性能，以期为后续换热器上镍基-不锈钢异种材料连接的焊接工艺的改进及生产制造提供试验依据 。……