杨维康等

【摘 要】通过对比试验的方法，研究了在混凝土中添加消泡剂和复掺磨细硅粉与粉煤灰对混凝土的密实度和表观质量的影响。通过测试和分析发现：分别添加消泡剂和复掺磨细硅粉与粉煤灰后自密实混凝土的密实度、表观质量及强度都得到了提高，然而采用既添加消泡剂又复掺磨细硅粉与粉煤灰的方法能使混凝土构件的密实度及表观质量得到双重提高，有利于提高混凝土的耐久性。

【关键词】自密实混凝土；消泡剂；硅粉；粉煤灰；密实度；表观质量

【中图分类号】TU528

【文献标识码】A

【Abstract】In the concrete is studied through contrast test， the method of adding defoaming agent and mixed grinding fine silicon powder and fly ash on the compactness of concrete and apparent quality. Through test and analysis found that： adding defoaming agent and mixed grinding fine silicon powder and fly ash after the compactness， apparent quality and strength of self-compacting concrete are improved， but the fine grinding of adding defoaming agent and mixed method of silicon powder and fly ash can make the compactness of concrete component and doubly improve apparent quality，to improve the durability of concrete.

【Key words】Self-compacting concrete；Foam resistance agent；Silica fume；Fly ash；Compactness；Apparent quality

1. 引言

（1）自密实混凝土（Self CompactingConcrete 或Self-Consolidating Concrete，简称SCC）是指在自身重力作用下，具有较好的流动性、密实性，即使存在致密钢筋也能完全填充模板，同时获得很好均质性，并且不需要附加振动的混凝土[1～3]。自密实混凝土属于绿色混凝土的范畴，是未来混凝土的发展方向之一。自密实混凝土在施工过程中的使用，可以减小由于机械广泛的振捣混凝土带来的噪声，减轻工人的劳动强度，避免管内危险作业和人为影响混凝土质量等，同时节约由于参与振捣的施工人员带来的经济负担；其具有良好的流动性、施工性能和填充性能，而且骨料不离析，混凝土硬化后具有良好的力学性能和耐久性，因此在未来的工程建设中将会得到广泛的运用[4～5]。

（2）随着混凝土技术的发展，自密实混凝土的应用越来越广泛，同时对混凝土的质量要求也越来越高。在实际工程条件下混凝土的现场浇筑不及实验室的条件理想，混凝土硬化之后表面存在蜂窝麻面的现象，未能达到较好的密实度和表观质量。……