【摘 要】采用Burgers模型研究沥青砂的粘弹性力学行为，研究粘弹性参数在沥青砂紫外光老化中的变化，分析其变化规律，评价沥青砂紫外光老化。确定紫外光老化的试验方法和沥青砂试件制作方法，对紫外光老化的沥青砂试件进行单轴压缩蠕变试验得到应变和时间的蠕变曲线，拟合了Burgers模型的四参数。对粘弹性参数随老化程度的变化规律进行研究，根据粘弹性参数随老化程度的变化研究沥青砂性能的变化规律。对不同老化程度和相应的Burgers模型四参数进行拟合得到粘弹性参数和老化程度h之间的表达式J（h），用该关系式表示沥青砂的老化程度。

【关键词】沥青砂；紫外光老化；粘弹性参数；蠕变试验；老化程度

【Abstract】Burgers model were carried out to study the viscoelastic mechanics behavior of tar sands. By researching the change of viscoelastic parameters in the ultraviolet aging tar sands， analyze its change regulation and evaluate its aging extent. Determine ultraviolet aging test method and asphalt sand specimen producing method. Put the ultraviolet aging of asphalt sand specimen in uniaxial compression creep test to get the creep curves of strain and time， using the least squares fitting of the four parameters of Burgers model. Fitting the aging degree and the corresponding model parameters fitting， get the relation between viscoelastic parameters and aging degree and get the expression J （h） between creep compliance J and aging degree of， The aging of asphalt sand was expressed with J （h）.

【Key words】Asphalt mastic；Ultraviolet Radiation aging；Viscoelastic Parameters； creep test；Aging index

沥青路面老化的研究中最早引起关注的是沥青结合料本身，对沥青砂和沥青混合料的抗老化性能研究较少，至今仍没有评价其老化性能的标准试验方法[1，2]，应提出合理的老化试验方法和评价指标。针对沥青砂进行研究，考虑沥青砂的流变特性，从其粘弹性角度，研究沥青砂的老化性能。沥青混合料和沥青砂具有相似的压缩变形和蠕变变形曲线，本文进行的基于粘弹性参数的沥青砂老化程度研究可以为沥青混合料紫外光老化程度的研究提供依据。

1. 沥青混合料紫外光老化试验

1.1 老化试件制作。

试验采用沥青砂AS-16作为研究对象，其中沥青采用SBS改性沥青，集料为从拌合厂提取的机制砂经过筛分后得到粒径小于2.36mm的砂粒。沥青砂AS-16的级配按照规范中规定AC-16相应的细集料（粒径2.36mm）的相同比例进行设计，AC-16级配如表1，AS-16的级配如表2。……