摘要: 近年来，随着基础设施建筑规模不断扩大，大型现代化技术设施或结构物不断增多，如何保工程质量、施工技术的合理运用是至关重要。如何采取有效措施防止大体积混凝土的开裂与保持混凝土结构密实程度，是一个值得关注的问题。本文简述了大体积混凝土裂缝形成原因及施工方法,从合理选择混凝土配合比、严格控制混凝土入模温度等方面,提出了保证大体积混凝土施工质量的控制措施。

关键词:裂缝;混凝土浇筑;施工技术

Abstract: in recent years, as infrastructure construction continues to expand the scale of large-scale modern technology facilities or structures growing, how to the engineering quality, construction technology is reasonable apply is crucial. How to take effective measures to prevent massive concrete crack in the concrete structure and keep close-grained degree, is a concern. This paper briefly describes the mass concrete crack formation reasons and construction method, from the rational choice concrete, strictly control the mode of concrete temperature and so on, proposed guarantee mass concrete construction quality control measures.

Keywords: crack; Concrete casting; Construction technology

中图分类号： TV544+.91文献标识码：A文章编号：

一、大体积混凝土裂缝形成的原因

裂缝产生的原因可分为两类：一是结构型裂缝，是由外荷载引起的，包括常规结构计算中的主要应力以及其他的结构次应力造成的受力裂缝。二是材料型裂缝，是由非受力变形变化引起的，主要是由温度应力和混凝土的收缩引起的。本文主要探讨材料型裂缝。其中具体原因如下。

1.1 温度应力引起裂缝（温度裂缝）

目前温度裂缝产生主要原因是由温差造成的。温差可分为以下三种：混凝土浇注初期，产生大量的水化热，由于混凝土是热的不良导体，水化热积聚在混凝土内部不易散发，常使混凝土内部温度上升，而混凝土表面温度为室外环境温度，这就形成了内外温差，这种内外温差在混凝土凝结初期产生的拉应力当超过混凝土抗压强度时，就会导致混凝土裂缝；另外，在拆模前后，表面温度降低很快，造成了温度陡降，也会导致裂缝的产生；……