摘要：近年来,随着国家建设的需要,高层建筑的地下室工程正迅猛发展。但由于地下室多采用钢筋混凝土结构,其不仅会使混凝土中的钙大量流失;同时还会使混凝土中的钢筋锈蚀,从而破坏了地下混凝土结构的整体性,进而影响了主体结构的稳定性和使用寿命。因此,从地下室防水技术中常见问题，提出对高层建筑地下室防水的质量控制。

关键词：高层建筑；地下室；防水

Abstract: In recent years, along with the needs of national construction, high-rise building basement engineering is developing rapidly. But because the basement use of reinforced concrete structures, which not only makes a huge loss of calcium in concrete; at the same time will make the steel corrosion in concrete, thus destroying the integrity of the underground concrete structure, thereby affecting the main structure, stability and service life. Therefore, from the basement waterproof technology problems, and put forward to basement waterproofing of high-rise building quality control.

Key words: high-rise building; waterproof basement;

中图分类号：TU745.3文献标识码：A文章编号：2095-2104（2012）05-0020-02

一、地下室防水技术问题

1、混凝土养护

大体积混凝土的内外温差大，必须做好养护工作。本工程浇筑时气温高达35°，只进行保湿养护。采用浇水养护并覆盖塑料薄膜，防止混凝土水份蒸发和表面脱水而产生干缩裂缝，养护时间不少于14d。

2、混凝土的泌水处理

大体积大流动性混凝土在浇筑和振捣中，上涌的泌水和浮浆会跟着混凝土坡面流到坑底，并随混凝土向前推进。在支模时，应在混凝土浇筑前进方向二侧模底部留孔排出泌水和浮浆。当混凝土坡脚接近尽端模板时，要立即改变混凝土浇筑方向，由尽端往回浇，另外加强二侧混凝土的浇筑，使最后混凝土的浇筑形成四面会合，这样泌水和浮浆可以集中排除。

3、混凝土的表面处理

大体积泵送混凝土，排除泌水和浮浆后，表面仍有较厚的水泥浆，在浇完4～5h后，要用长括尺括平，在初凝前用滚筒来回碾压数遍，待接近终凝前，用木蟹再打磨一遍，使收水裂缝闭合。