LDPE含量对LLDPE/LDPE共混物性能的影响

秦小梅，李树材，李 邦

(天津科技大学材料科学与化学工程学院，天津 300457)

以线性低密度聚乙烯(LLDPE)与低密度聚乙烯(LDPE)为原料，经Brabender挤出机熔融吹膜制备出LLDPE/LDPE共混膜，并借助差示扫描量热仪(DSC)、偏光显微镜(POM)、电子万能试验机和毛细管流变仪研究了LLDPE/LDPE共混物的结晶行为、结晶形态、力学性能以及熔体流变性能．结果表明：加入适量LDPE后，共混膜仍然具有较好的综合力学性能．随着LDPE质量分数的增加，共混物的结晶度下降，晶粒尺寸减小；共混物的熔体流变性能提高．

线性低密度聚乙烯；低密度聚乙烯；共混膜；结晶；力学性能；流变

Abstract：Linear low density polyethylene(LLDPE)/low density polyethylene(LDPE)blend film was prepared through melt blow ing by Brabender extruder. The crystallization behavior and crystal morphology of the blend were characterized by DSC and POM. In addition，mechanical properties and melt rheological properties of the blend film were investigated. The results indicate that the comprehensive mechanical properties of the blend film can still keep fine after adding appropriate amount LDPE. The crystallinity and grain size of the blend decrease and melt rheological properties are improved w ith the increase of LDPE.

Keywords：LLDPE；LDPE；blend film；crystallization；mechanical properties；rheological

线性低密度聚乙烯(LLDPE)是20世纪70年代开发成功的乙烯与α–烯烃的共聚物，其分子呈线型结构，分子链上含有一定数量的短支链，分子链之间堆砌较为规整，结晶度较高，因此其拉伸强度、撕裂强度、耐穿刺性和断裂伸长率均较高，具有良好的综合性能[1–7]．由于这些突出优点，LLDPE广泛用于制备各种薄膜．尽管如此，LLDPE薄膜也存在不足，如较高的结晶度导致薄膜的透明性较差；较短的支链和较窄的相对分子质量分布使LLDPE熔体黏度高，比熔体流动速率相同的LDPE更难加工[8]．而LDPE透明性好，易于加工，因此，若在LLDPE中混入一定量LDPE，则可改善其光学性能与加工性能．

本文将LLDPE与LDPE按不同配比共混，制备出共混薄膜，研究了LDPE质量分数对LLDPE/LDPE共混膜的结晶性能、结晶形态、力学性能以及熔体流变性能的影响．