刘瑜帅

摘 要：针对传统装裱工艺中粘胶剂的缺陷，对传统的装裱材料进行改进，将传统的添加物明矾换成纳米ZnO和NaHCO3，进而分别探讨以上两种添加剂对装裱的影响。结果表明，纳米ZnO+NaHCO3结合传统浆糊在热老化条件下pH值接近中性，且在低温下表现出良好的固化作用。

关键词：装裱书法;纳米ZnO;固色性能;热老化

中图分类号：TQ437 文献标识码：A     文章编号：1001-5922（2021）10-0022-03

Preparation， Performance and Application of Adhesive in Calligraphy Mounting

Liu Yushuai

（Academy of Fine Arts， Xianyang Normal University， Xianyang 712000， China ）

Abstract：Aiming at the defects of the adhesive in the traditional mounting process， the traditional mounting materials are improved， and the traditional additive alum is replaced with nanometer ZnO and NaHCO3 ， and then the influence of the above two additives on mounting is discussed separately. The results show that the pH value of nano-ZnO+NaHCO3 combined with traditional paste is close to neutral under heat aging conditions， and it exhibits a good curing effect at low temperatures.

Key words：mounted calligraphy; nano-zno; fixing performance; thermal aging

浆糊作为中国传统书法装裱技术中的粘胶剂，由面粉加热制成，是装裱过程中不可或缺的材料，因此其质量对装裱效果有着至关重要作用。中国现代装裱工艺中粘胶剂大多由浆糊和明矾所制，但研究表明，采用浆糊和明矾制作的粘胶剂对书法作品进行装裱，会给作品带来一定影响。因此，针对以上问题，对传统装裱工艺中的主要材料（浆糊）进行改良，研究不同添加剂的浆糊对装裱效果产生的影响。而通过本研究，期望得到一种环保的、固色效果好的、可用于紙张文物保护的新型粘胶剂。

1 材料与方法

1.1 材料与设备NaHCO3

宣纸（安徽红星造纸厂）、浆糊（实验室自制）、明矾（天津市科密欧化学试剂开发中心，分析纯）、纳米ZnO粉末（舟山明日纳米科技有限公司，分析纯）、NaHCO3粉末（天津市天力换血试剂有限公司，分析纯）、蒸馏水（实验室自制）、墨汁（河东区春溪文化用品厂，工业级）。

UV灯管（东莞市尔谷光电科技有限公司，260W）、小型坩埚（郑州科瑞（集团）耐火材料有限公司）、耐折度测定仪（长春市月明小型实验机有限责任公司，MIT）、全自动色差仪（北……