朱华娟 贾荣斌

摘 要：从固化时间、剪切强度、金属腐蚀结果的影响等方面进行了系统研究，分析了改变缓蚀剂用量对丙烯酸酯胶腐蚀效果的影响。结果表明，当缓蚀剂苯丙三氮唑占到反应系统总剂量的1.5%时，丙烯酸酯胶固化时长为15.5min，剪切强度为16.6MPa，对铜的单位面积侵蚀为32%。

关键词：缓蚀剂;固化时间;剪切强度

中图分类号：TQ433.4+3 文献标识码：A     文章编号：1001-5922（2021）10-0001-02

Study on the Effect of Corrosion Inhibitor on the Properties of Acrylate Adhesive

Zhu Huajuan1， Jia Rongbin2

（1.Xiangyang Safety Production Publicity and Education Information Center， Xiangyang 441021，China;2.Logistics Service Center of Xiangyang Economic and Information Technology Bureau， Xiangyang 441003， China）

Abstract：In this paper， the effects of different inhibitor dosage on the properties of acrylate adhesive were studied， and the changes of curing time， shear strength and metal corrosion effect were analyzed and discussed. The results showed that when the corrosion inhibitor phenylprotriazole accounted for 1.5% of the total dosage of the reaction system， the curing time of the acrylic adhesive was 15.5min， and the corrosion effect on copper per unit area was 32%.

Key words：corrosion inhibitor; curing time; shear strength

0 引言

丙烯酸酯膠因固化速度快、强度高、粘接性好的特点在各工业领域中得到广泛应用，但因该物质在生产过程中，反应物含有甲基丙烯酸铜等，致使生成物的表面产生腐蚀瘢痕，限制了该产品的使用。本研究以最大限度降低金属表面腐蚀面积，同时使得胶体综合性能保持较好水平 [1]为目标，对降低胶体缓蚀剂量采取逐步增加措施，针对性的在丙烯酸酯胶中加入缓蚀剂，观察其添加剂量与腐蚀面积关系确定比例、剂量，达到预期效果。

1 实验材料和方法

1.1 主要原料

甲基丙烯酸羟乙酯（HEMA）、甲基丙烯酸甲酯（MMA）、甲基丙烯酸、苯丙三氮唑（缓蚀剂）、异丙苯过氧化氢、羧基丁腈橡胶（NBR）、工业硫脲、阻聚剂、增韧助剂，市售。

1.2 试验设备

炼胶机，行星真空混合机，高速分散机，万能电子拉力机。

1.3 制备方法

1.3.1 甲组分的制备

（1）将NBR在开炼机上塑炼，薄通10次后出片，备用。

（2）按照配比数量，将甲基丙烯酸、苯丙三氮唑、MMA、NBR、HEMA、增韧助剂等原料先后投入到反应釜内，经搅拌，至原料完全溶解。

（3）加入四甲基硫脲促进剂搅拌均匀待用。

1.3.2乙组分的制备

（1）按配比，先后将甲基丙烯酸羟乙酯（HEMA）、阻聚剂、甲基丙烯酸羟甲酯（MMA）、丁腈橡胶（NBR）等质料投入到反应釜中，充实搅拌，至全部物料彻底消融。……