摘 要：研究以高分子聚合物混凝土增强剂为对象分析了硫酸钠掺量对不同类型增强剂的性能影响。经实验研究发现，在高分子聚合物混凝土增强剂中加入适量的乳胶粉和硫酸钠并将其涂抹在混凝土表面，能够显著提升混凝土强度。

关键词：凝土增强剂;高分子聚合物;硫酸钠

中图分类号：TU528 文献标识码：A 文章编号：1001-5922（2021）07-0034-04

Analysis of the Influence of Sodium Sulfate Content on the Performance of High Molecular Polymer Concrete Reinforcing Agent

Li Yanling1， Li Junyang2

（1.Shaanxi Polytechnic Institute， XianYang 712000， China;2.Shaanxi Road and Bridge Group Pavement Engineering Co.， Ltd， Xi an 710054， China）

Abstract：In this study， the effect of sodium sulfate content on the performance of different types of reinforcing agents was analyzed based on the high-molecular polymer concrete reinforcing agent. Experimental studies have found that adding proper amount of latex powder and sodium sulfate to the high-molecular polymer concrete reinforcer and applying it on the concrete surface can significantly improve the concrete strength.

Key words：concrete reinforcing agent; high molecular polymer; sodium sulfate

在水泥材料中加入适量的混凝土增强剂能够一定程度上提升混凝土结构的致密性，混凝土增强剂的主要成分通常为高分子聚合物，该物质与混凝土发生化学反应后能够起到熟化封堵的效果，较久地锁住孔隙[1-3]，从而得到耐候耐久、抗裂、抗压、高强、坚固和抑制部分工业化学品侵蚀的结构表面。由于高分子聚合物的使用成本较高，因此许多施工单位会采用混凝土增强剂配合碳酸钠的混凝土强化方法 [4-8]。然而，有些施工单位为了节省施工成本，过多地使用碳酸钠代替混凝土增强剂，进而造成混凝土的碱骨料反应，给施工现场造成了一定的安全隐患[9-13]。为了最大程度上强化混凝土结构的性能，本次研究通过实验的方式对碳酸钠的合理用量进行分析。

1 实验材料

本次研究所使用的水泥材料为力顿公司生产的常规轻集料混凝土;所使用的高分子聚合物混凝土增强剂分别为晶顿公司生产的锂基渗透液、道康宁公司生产的6683有机硅树脂乳液和恒宇公司生产的水性环氧树脂乳液DY-128-50;所使用的乳胶粉为SAE乳胶粉，其主要的化学成分是丙烯酸酯系共聚物;所使用的硫酸钠为普通工业硫酸钠，其主要的化学成分是Na2SO4·10H2O。……