刘松岸 刘亚飞

摘 要：文章主要通过实验研究的方法，对再生轮胎橡胶混凝土的压缩强度、弯曲强度、轴心压缩强度、弹性模量及其徐变性能进行分析。实验结果表明，当橡胶颗粒掺量和再生粗骨料不断增加时，混凝土的压缩强度、弯曲强度、轴心压缩强度和弹性模量均处于不断下降趋势，徐变表现为增加趋势;当橡胶颗粒掺量大于10%之后，前四项力学性能下降速率加快;当橡胶掺量和环境相对湿度降低时，混凝土的徐变速率不断增加。

关键词：再生轮胎橡胶混凝土;力学性能;徐变性能

中图分类号：TQ335 文献标识码：A 文章编号：1001-5922（2021）07-0017-04

Research on Recycled Tire Rubber Concrete and Its Creep Performance

Liu Songan， Liu Yafei

（The Engineering&Technical College of Chengdu University of Technology， Leshan 614000， China）

Abstract：This paper mainly analyzes the compressive strength， flexural strength， axial compressive strength， elastic modulus and creep properties of recycled tire rubber concrete through experimental research methods. The experimental results show that when the content of rubber particles and recycled coarse aggregates continue to increase， the compressive strength， flexural strength， axial compressive strength and elastic modulus of concrete are all in a downward trend， and creep shows an increasing trend; when the amount of rubber particles is greater than 10%， the first four mechanical properties decrease at a faster rate; when the amount of rubber and the relative humidity of the environment decrease， the creep rate of concrete increases continuously.

Key words：recycled tire rubber concrete; mechanical properties; creep properties

混凝土作為建筑工程中的主要材料，发挥极为重要的作用，并且随着社会发展其使用量不断增加[1]。加工混凝土需要大量的沙石粗料，往往会以破坏生态环境大量开采这些原材料，如今提倡节能环保、可持续发展，必须减少这些不可再生能源的使用[2-3]。为了解决这个问题，使用绿色环保可再生的替代材料用于混凝土制作中，能够在一定程度降低沙石的使用量[4-5]。于是发现再生轮胎橡胶能够作为细骨料替代沙石，但是在使用该材料的同时，不能降低混凝土的使用性能[6-8]。于是文章对再生轮胎橡胶混凝土及其徐变性能进行研究，从而更加深入了解再生轮胎橡胶混凝土的性能。

1 实验过程

1.1 实验材料

实验需要的主要材料有：水泥、水、C30混凝土、天然石子、粗骨料、细骨料等，其中细骨料主要包含天然河沙和橡胶颗粒，橡胶颗粒主要使用的回收废旧轮胎进行加工，使之成为颗粒状态。……