摘 要：浇注件生产过程复杂，工艺控制困难。浇注件的生产过程容易出现气泡、开裂、缺陷、玻璃化温度不合格等质量问题。本文就产生这些质量问题的原因一一进行阐述。在实际生产中，要选择合适的原材料，配合较优的浇注件、嵌件、模具设计，严格进行工艺控制，合理进行装脱模操作，保证浇注件的各项性能指标都能满足要求。

关键词：浇注件;气泡;模具;爆聚

中图分类号：TM412 文献标识码：A 文章编号：1003-5168（2021）29-0063-03

Analysis on Common Quality Problems and Causes of Epoxy Resin Castings

ZHANG Jing DONG Baoying LI Yongkui CHEN Rui LU Yinhua

（Henan Pinggao Electric Co.， Ltd.， Pingdingshan Henan 467001）

Abstract： The production process of the casting is complicated and the process control is difficult. The production process of castings is prone to quality problems such as bubbles， cracks， defects， and unqualified glass transition temperature. This paper explains the reasons for these quality problems one by one. In actual production， it is necessary to select appropriate raw materials， cooperate with better pouring parts， inserts， and mold designs， strictly control the process， and perform reasonable assembly and demolding operations to ensure that the performance indicators of the pouring parts meet the requirements.

Keywords： casting parts;bubble;mould;explosive polymerization

高压开关设备用环氧浇注绝缘制品要求外观完美，尺寸稳定，机、电、热性能满足产品要求[1-5]。目前普遍采用真空浇注成型技术，要点是去除浇注制品内部和表面的气泡，减少内部应力，防止产生裂纹等。为了达到目的，必须选用合适的浇注材料，使用适宜的真空浇注设备，严格控制原材料的预处理、混料、澆注和固化过程，采用合理的设计模具和正确的操作步骤等[6-9]。图1为环氧树脂真空浇注成型的工艺流程。

环氧树脂浇注绝缘件是高压开关设备的关键构件。绝缘件各项性能的稳定至关重要，关系着整台电气设备的安全与稳定[10-12]。随着超高压、特高压电网的推广应用，输变电设备的质量稳定性显得日益重要。然而，在浇注件的实际生产中也存在相应的问题。浇注件容易出现的质量问题主要表现为气泡、缺陷及玻璃化温度不合格等[13-16]。笔者就这些质量问题及产生原因进行简要分析。

1 气泡

产生气泡的原因有很多，主要可归结为5个方面。……