赖春明 李昭赞 陈静 李卡

【摘  要】论文提出将硼酸、氢氧化钠、硅溶胶、甲基纤维素按配置制成水溶液作为防燃涂料，并通过设计正交试验优化各成分的配比为10：6：10：7。结果表明，在制壳之前将防燃涂料涂挂在白模表面可有效形成防燃涂层，在镁合金消失模-壳型复合铸造过程中能有效地发挥镁液的防燃效果。

【Abstract】The paper proposes that boric acid， sodium hydroxide， silica sol， and methylcellulose are made into an aqueous solution as a flame-retardant coating according to the configuration. The ratio of each component was optimized by designing an orthogonal experiment to be 10：6：10：7. The results show that the flame-retardant coating can be effectively formed by hanging the flame-retardant coating on the surface of white mold before shell making， and the flame-retardant effect of magnesium solution can be effectively exerted in the process of magnesium alloy expendable pattern-shell compound casting.

【关键词】消失模-壳型复合铸造;防燃;涂层;镁合金

【Keywords】expendable pattern-shell compound casting; flame-retardant; coating; magnesium alloy

【中图分类号】TG249.5                               【文献标志码】A                                   【文章编号】1673-1069（2020）07-0180-02

1 引言

镁合金具有质量轻、比强度高、抗震性好、铸造性能好等优点，但其塑性成形能力较差，所以目前实际应用的镁合金零件主要是铸造成型为主。镁的化学性质非常活泼，如何阻止或降低铸造成型过程中镁液与铸型界面的燃烧反应是镁合金铸造工艺应用过程中的关键问题之一，直接关系着铸件的表面质量。

目前，镁和镁合金在铸造成型过程中阻止镁液与铸型界面之间反应的主要方法有以下几种：一是在铸型中通入可以阻燃的保护气体，阻止镁液与铸型的直接接触;二是通过铸型的涂层在高温下生成保护气体;三是对铸型本身加以保护，可以通过形成性质稳定的釉质保护膜来隔绝镁液与铸型界面的直接接触，或采用不与镁发生反应的材料制作铸型和耐火层。本研究在前人研究的基础上，利用正交试验配置了一种基于硼酸的防燃膜涂料，起到了防止镁合金与铸型界面燃烧反应的作用。

2 实验材料与方法

大量的实验研究表明……