金雪

摘 要：本文通过分析混凝土强度检测的重要性，参照相关质量规范，结合工程实例，运用四类强度检测方法研究混凝土结构实体验收评定，对比分析测试结果，证实在50 mm直径芯样28 d等效龄期内，能代表标准芯样检测结构实体混凝土强度，对于75 mm直径芯样90 d等效龄期内，能代表标准芯样完成实体混凝土结构强度检测，为类似研究提供参考。

关键词：混凝土;结构实体;强度检测

中图分类号：TU755.7文献标识码：A文章编号：1003-5168（2020）19-0101-02

Abstract： In this paper， through the analysis of the importance of concrete strength detection， referring to the relevant quality standards， combined with engineering examples， four kinds of strength detection methods were used to study the acceptance evaluation of concrete structure entity. The test results were compared and analyzed. It is confirmed that within the 28 d equivalent age period of 50 mm diameter core sample， it can replace the standard core sample to detect the structural solid concrete strength. For 75 mm diameter core sample， 90 In the equivalent age of D， it can represent the standard core sample to complete the strength test of solid concrete structure， which provides reference for similar research.

Keywords： concrete;structural entity;strength testing

混凝土强度指在混凝土成型后，材料起主要决定性作用的混凝土的最大承载力。对建筑行业来说，混凝土强度是控制施工质量的关键影响因素[1]。若无法保证混凝土强度最终达标，那么自然也无法保证混凝土建筑安全性、稳固性达标[2]。所以，加强混凝土强度的检测意义重大。一般来说，混凝土强度主要指混凝土凝固后所能承受的最大荷载标准。目前，混凝土被广泛应用于各行业领域建筑工程中[3]，因此，对建筑工程来说，加强混凝土强度的检测至关重要。混凝土强度检测方法较多，本文主要结合工程实例，对比分析不同混凝土结构实体强度检测方法。

1 试验材料与方法

1.1 原材料

在本次试验中运用普通硅酸盐水泥，参数详见表1。选用天然河沙，该河沙的参数为：2.5%含泥量，0.8%泥块含量。共选用两类石子，一种石子含泥量为0.7%，泥块含量为0.3%，最大粒径为31.5 mm，空隙率为4.6%;另一种石子含泥量为0.7%，泥块含量为0.3%，最大粒径为20 mm，空隙率为42%。粉煤灰为F类别，细度为18.2%和需水量为104 m3，烧矢量为1.97%;S95级矿渣粉的流动度比为97%，比表面积为436 m2/kg。……