王敏 姜瑞雨 宋欣钰

摘      要：为了研究硫转移剂助剂在石油冶炼工程中的脱硫效果，通过共沉淀法添加葡萄糖软模板助剂合成纳米级镁铝尖晶石，在此基础上添加铁元素合成的三元复合金属氧化物。结果表明镁铝尖晶石添加葡萄糖模板剂后的最优吸附脱硫效果比未添加的提高约31.03%;添加铁元素后的最佳脱硫效果比未添加的提高约10.81%。可见添加软模板助剂的含铁型催化裂化再生烟气硫转移剂能够有效提高其吸附脱硫效果。

关  键  词：硫转移剂;共沉淀;软模板;催化裂化关键词1;关键词2;关键词3;关键词4

中图分类号：TE6TQ 000       文献标识码： A       文章编号： 1671-0460（2020）04-0548-05

Abstract： In order to research the desulfurization effect of sulfur transfer agent in petroleum refining project， the synthesis of nanometer magnesia-alumina spinel by adding glucose soft template additive was studied by coprecipitation method， and then ternary compound was synthesized by adding iron element. The results showed that the optimum adsorption desulfurization effect of magnesium aluminate spinel after adding glucose template was about 31.03% higher than that without glucose template; the optimum desulfurization effect after adding iron element was about 10.81% higher than that without iron element. So the iron-containing catalytic cracking regeneration flue gas sulfur transfer agent with soft template auxiliary can effectively improve the adsorption desulfurization effect.

Key words： Sulfur transfer agent; Total precipitation; Soft template; Catalytic cracking

隨着中国特色社会主义科学发展观理念的不断深入，加强生态建设和环境保护，推动绿色发展成为人们关注的重点。而在石油冶炼工业中[1]，增加重质原料油会导致催化裂化（FCC）工艺反应过程中积聚到催化剂上的焦炭和杂质增多，原油中的硫50%以上都能够转化为硫化氢，继而随FCC再生烟气排放到大气中，造成一定的污染[2]。这就对FCC工艺中硫化物排放提出了限制及更高的要求。目前能够有效控制硫化物排放的途径有原料加氢脱硫和烟气洗涤技术，但成本颇高，所以廉价的硫转移剂技术亟须快速发展并投入使用。

硫转移剂经历了从氧化物到镁铝尖晶石再到现在的类水滑石阶段，通过氧化脱硫和还原再生实现硫转移剂的循环脱硫。氧化脱硫过程在500 ℃再生器中进行，硫转移剂伴随主催化剂循环进入FCC反应器中，反应器中存在大量的低碳烃类、氢气及蒸汽，这些气体可以用来实现硫转移剂的还原再生。……