王红军，陈 洋，方旭旭，华 香，杨术明

（信阳师范学院化学化工学院，河南信阳464000）

氟/膨润土/锡酸钙复合光催化剂的制备及光催化性能*

王红军，陈 洋，方旭旭，华 香，杨术明

（信阳师范学院化学化工学院，河南信阳464000）

采用水热合成法制备出氟掺杂膨润土负载锡酸钙复合光催化剂，采用X射线衍射（XRD）、扫描电子显微镜（SEM）等分析手段对样品的形貌和结构进行了表征，并在可见光条件下考察了催化剂用量、氟掺杂量、反应时间等因素对复合光催化剂降解亚甲基蓝废水溶液性能的影响。结果表明：氟掺杂量为0.04%（质量分数）时复合光催化剂对亚甲基蓝溶液的降解效果最好，当催化剂质量浓度为60 mg/L，反应时间为13 min时，其对亚甲基蓝溶液的降解率可达98.6%。

氟掺杂；CaSnO3；复合光催化剂；光催化降解

Abstract：Fluorine/bentonite/CaSnO3composite photocatalysts were prepared by hydrothermal synthesis method.The morphology and structure of samples were characterized by X-ray diffraction（XRD)and scanning electron microscope（SEM）etc..The effects of light catalyst dosage，fluorine-doping ratio，and reaction time on photocatalytic activity of methyl blue waste water were also investigated.Results indicated that the photo-degradation efficiency could reach 98.6%when the fluorinedoping ratio was 0.04%（mass fraction），the mass concentration of photocatalyst was 60 mg/L，and the reaction time was 13 min.

Key words：fluorine doping；CaSnO3；composite photocatalyst；photocatalytic degradation

近年来催化剂的应用非常广泛，催化剂的研究及开发逐渐成为现代化学工业的核心问题之一［1］。在催化剂的发展过程中，光催化剂因可将大多数污染物降解，且不会产生新的污染，受到人们的日益重视［2-3］。当前，光催化剂的研究主要集中在二氧化钛、氧化锌等方面，大部分光催化剂的颗粒粒径较小，催化剂在溶液中很容易团聚，使催化剂的表面积减小，催化效率降低。人们总是不断改进催化剂的制备方法和原料组成等，以期得到催化效果更优良，且成本低、无污染的催化剂。

CaSnO3属于钙钛矿型氧化物ABO3，是一种具有特殊理化性能的非金属材料，这类材料本身前两位元素均易被一些其他金属或非金属元素全部取代或部分取代，具有较稳定的晶体结构及高电子流动性、高导电率和光电特性等，作为一种新型材料被广泛应用于环境保护和工业催化等众多领域［4-5］。……