黄义芳+陈维富+蒋勇+朱平+赵建仓+郭晓凯+黄腾飞+邱振生

苏州 215004；3.中广核工程有限公司，广东 深圳 518124）

摘要： 针对核电用低合金钢焊条CHE608HR2，采用改变焊接热输入的方法，借助金相显微镜，研究了焊接热输入对其熔敷金属力学性能及组织的影响。结果表明，熔敷金属力学性能随着焊接热输入量增大而降低，焊接热输入大于32 kJ/cm时，熔敷金属力学性能下降明显；焊接热输入小于等于25 kJ/cm时，熔敷金属力学性能最优。

关键词： 熔敷金属； 焊接热输入； 力学性能

中图分类号： TG422

Abstract：The influence of welding heat input on the mechanical properties and microstructure of the alloy was studied by means of metallographic microscope， the CHE608HR2 of low alloy steel for nuclear power and the method of changing the heat input. The results show that the mechanical properties of the weld metal are decreased with the increase of the welding heat input， and the mechanical properties of the welded metal are decreased obviously， while the welding heat input is less than or equal to 25 kJ/cm， and the mechanical properties of the weld metal is the best.

Key words：weld metal； heat input； mechanical properties

0 前言

近几年国内核电行业迅速发展，随着国内三代核电机组的陆续开工，对三代核电机组用焊接材料的需求也与日俱增，低合金钢焊条作为三代核电机组用焊接材料的重要组成部分[1-4]，为了更好的应用于核电工程，文章的试验焊条为国家能源局“核级焊接材料国产化开发及应用研究”项目中的低合金钢焊条，牌号为CHE608HR2（型号为E9018-G），文章通过对焊条CHE608HR2改变焊接热输入的方式，研究对其熔敷金属的力学性能的影响，对工程应用具有一定的指导意义。

1 试验材料与方法

1.1 试验材料 试验焊条CHE608HR2熔敷金属的化学成分见表1。

“核级焊接材料国产化开发及应用研究”项目技术条件对试验焊条CHE608HR2熔敷金属常温力学性能的要求见表2。

1.2 试验设备

直读光谱仪：德国斯派克 SPECTROLAB M10；

微机控制电子拉力材料试验机：深圳瑞格尔 RGM4100；

摆锤式冲击试验机：美特斯 ZBC 3302C；

箱式电阻炉：天津泰斯特 SX410；

红外测温仪：上海世禄仪器 66/68；

焊机：时代逆变 ZX7400。

1.3 试验方法