卷取温度对45带钢组织和性能影响的实验研究

高锐夏志升张振申王中岐

( 安阳钢铁集团有限责任公司 )

研究了不同的卷取温度对45带钢组织和性能的影响，结果表明：随卷取温度的升高，试验钢的强度和硬度降低，塑性提高，且变化幅度较大；当卷取温度在珠光体转变开始温度以上时，产品组织为近似平衡转变的铁素体和珠光体组织，该钢具有较低的强度、硬度和优异的塑性特点，提高了产品的加工性能。

卷取温度45组织性能

ABSTRASTIn this paper, the microstructure and properties of 45 strips by different coiling temperature is studied. The results showed that, the strength and hardness of the experimental steel was reduced, and the toughness was improved, as coiling temperature was increased, and the variation was greatly. When coiling temperature above the pearlite transformation temperature, the product organization was ferrite and pearlite, as changed under the balance. The strength and hardness was low, the plasticity was high, and the processing properties were well.

0　前言

45钢由于其综合机械性能好，是生产中常用的材料之一，在齿轮、连接杆、蜗杆、叶轮、泵、活塞、曲轴等零件制造中广泛应用。对于薄规格45钢板，一般采用中厚板轧机上轧制生产，但薄规格产品的空冷速度大，导致热轧后产品的强度和硬度都高，后续加工难度很大，需要采用热处理工艺降低热轧产品的强度和硬度，造成生产成本较高。热连轧机组轧制生产的钢卷具有保温缓冷的特点，使钢卷的冷却速率降低，带钢达到近似回火热处理的作用，使产品的强度、硬度降低，产品的加工性能提高，热轧后的产品可直接加工，可省去加工前的热处理工序。另外，热连轧生产带钢时，可通过调节卷取温度控制产品的组织配比，使钢卷具有不同的性能，满足不同用途的需要。对薄规格45钢板，进行了热连轧生产线生产的实验研究。

1　实验方法

1.1实验方法

按照标准GB/T 711-2008的规定，45钢的化学成分要求见表1。……